Light-emitting element

ABSTRACT

A light-emitting element having high external quantum efficiency is provided. A light-emitting element having low drive voltage is provided. Provided is a light-emitting element which includes a light-emitting layer containing a phosphorescent compound, a first organic compound, and a second organic compound between a pair of electrodes. A combination of the first organic compound and the second organic compound forms an exciplex (excited complex). An emission spectrum of the exciplex overlaps with an absorption band located on the longest wavelength side of an absorption spectrum of the phosphorescent compound. A peak wavelength of the emission spectrum of the exciplex is longer than or equal to a peak wavelength of the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. application Ser. No. 15/492,439, filed Apr. 20, 2017, now pending, which is a continuation of U.S. application Ser. No. 14/924,054, filed Oct. 27, 2015, now U.S. Pat. No. 9,634,279, which is a continuation of U.S. application Ser. No. 13/419,892, filed Mar. 14, 2012, now U.S. Pat. No. 9,175,213, which claims the benefit of a foreign priority application filed in Japan as Serial No. 2011-064553 on Mar. 23, 2011, all of which are incorporated by reference.

TECHNICAL FIELD

The present invention relates to light-emitting elements using an organic electroluminescence (EL) phenomenon (hereinafter such light-emitting elements are also referred to as organic EL elements).

BACKGROUND ART

An organic EL element has been actively researched and developed. In a fundamental structure of the organic EL element, a layer including a luminescent organic compound (hereinafter also referred to as light-emitting layer) is interposed between a pair of electrodes. The organic EL element has attracted attention as a next-generation flat panel display element owing to characteristics such as feasibility of being thinner and lighter, high speed response to input signals, and capability of direct current low voltage driving. In addition, a display using such a light-emitting element has a feature that it is excellent in contrast and image quality, and has a wide viewing angle. Further, being a planar light source, the organic EL element has been attempted to be applied as a light source such as a backlight of a liquid crystal display and a lighting device.

The emission mechanism of the organic EL element is of a carrier-injection type. That is, by application of voltage with a light-emitting layer interposed between electrodes, electrons and holes injected from the electrodes are recombined to make a light-emitting substance excited, and light is emitted when the excited state relaxes to the ground state. There can be two types of the excited states: a singlet excited state (S*) and a triplet excited state (T*). The statistical generation ratio of the excited states in a light-emitting element is considered to be S*:T*=1:3.

In general, the ground state of a light-emitting organic compound is a singlet state. Therefore, light emission from the singlet excited state (S*) is referred to as fluorescence because it is caused by electron transition between the same spin multiplicities. On the other hand, light emission from the triplet excited state (T*) is referred to as phosphorescence where electron transition occurs between different spin multiplicities. Here, in a compound emitting fluorescence (hereinafter referred to as fluorescent compound), in general, phosphorescence is not observed at room temperature, and only fluorescence is observed. Accordingly, the internal quantum efficiency (the ratio of generated photons to injected carriers) in a light-emitting element including a fluorescent compound is assumed to have a theoretical limit of 25% based on S*:T*=1:3.

On the other hand, when a compound emitting phosphorescence (hereinafter referred to as phosphorescent compound) is used, an internal quantum efficiency of 100% can be theoretically achieved. That is, higher emission efficiency can be obtained than using a fluorescent compound. For these reasons, a light-emitting element including a phosphorescent compound has been actively developed in recent years in order to achieve a high-efficiency light-emitting element. As the phosphorescent compound, an organometallic complex that has iridium or the like as a central metal has particularly attracted attention owing to their high phosphorescence quantum yield; for example, an organometallic complex that has iridium as a central metal is disclosed as a phosphorescent material in Patent Document 1.

When a light-emitting layer of a light-emitting element is formed using a phosphorescent compound described above, in order to suppress concentration quenching or quenching due to triplet-triplet annihilation in the phosphorescent compound, the light-emitting layer is often formed such that the phosphorescent compound is dispersed in a matrix of another compound. Here, the compound serving as the matrix is called host material, and the compound dispersed in the matrix, such as a phosphorescent compound, is called guest material.

REFERENCE Patent Document

[Patent Document 1] International Publication WO 00/70655 pamphlet

DISCLOSURE OF INVENTION

However, it is generally said that the light extraction efficiency of an organic EL element is approximately 20% to 30%. Accordingly, considering light absorption by a reflective electrode and a transparent electrode, the external quantum efficiency of a light-emitting element including a phosphorescent compound has a limit of approximately 25% at most.

Further, as described above, application of organic EL elements to displays and lightings has been considered. One of objects to be achieved here is a reduction in power consumption. In order to reduce power consumption, it is required to reduce the drive voltage of the organic EL element.

An object of one embodiment of the present invention is to provide a light-emitting element with high external quantum efficiency. Another object of one embodiment of the present invention is to provide a light-emitting element with low drive voltage.

Note that the invention to be disclosed below aims to achieve at least one of the above-described objects.

One embodiment of the present invention is a light-emitting element which includes a light-emitting layer containing a phosphorescent compound, a first organic compound, and a second organic compound between a pair of electrodes, in which a combination of the first organic compound and the second organic compound forms an exciplex, in which an emission spectrum of the exciplex overlaps with an absorption band located on the longest wavelength side of an absorption spectrum of the phosphorescent compound, and in which a peak wavelength of the emission spectrum of the exciplex is longer than or equal to a peak wavelength of the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound.

Another embodiment of the present invention is a light-emitting element which includes a light-emitting layer containing a phosphorescent compound, a first organic compound, and a second organic compound between a pair of electrodes, in which a combination of the first organic compound and the second organic compound forms an exciplex, in which an emission spectrum of the exciplex overlaps with an absorption band located on the longest wavelength side of an absorption spectrum of the phosphorescent compound, and in which a difference between a peak wavelength of the emission spectrum of the exciplex and a peak wavelength of an emission spectrum of the phosphorescent compound is 30 nm or less.

Another embodiment of the present invention is a light-emitting element which includes a light-emitting layer containing a phosphorescent compound, a first organic compound, and a second organic compound between a pair of electrodes, in which a combination of the first organic compound and the second organic compound forms an exciplex, in which an emission spectrum of the exciplex overlaps with an absorption band located on the longest wavelength side of an absorption spectrum of the phosphorescent compound, and in which a peak wavelength of the emission spectrum of the exciplex is longer than or equal to a peak wavelength of the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound and shorter than or equal to a peak wavelength of an emission spectrum of the phosphorescent compound. In addition, it is preferable that a difference between the peak wavelength of the emission spectrum of the exciplex and the peak wavelength of the emission spectrum of the phosphorescent compound be 30 nm or less.

Further, one embodiment of the present invention is the aforementioned light-emitting element in which the exciplex is formed from a singlet exciton of the first organic compound.

Further, one embodiment of the present invention is the aforementioned light-emitting element in which the exciplex is formed from an anion of the first organic compound and a cation of the second organic compound.

In the aforementioned light-emitting element, it is preferable that excitation energy of the exciplex be transferred to the phosphorescent compound, so that the phosphorescent compound emits phosphorescence.

In the aforementioned light-emitting element, it is preferable that at least one of the first organic compound and the second organic compound be a fluorescent compound.

In the aforementioned light-emitting element, it is preferable that the phosphorescent compound be an organometallic complex.

The light-emitting element of one embodiment of the present invention can be applied to a light-emitting device, an electronic device, and a lighting device.

According to one embodiment of the present invention, a light-emitting element having high external quantum efficiency can be provided. According to another embodiment of the present invention, a light-emitting element having low drive voltage can be provided.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 shows an absorption spectrum and emission spectra according to Example 1.

FIG. 2 shows an absorption spectrum and emission spectra according to Example 1.

FIG. 3 shows an absorption spectrum and emission spectra according to Example 1.

FIG. 4 shows an absorption spectrum and emission spectra according to Example 1.

FIG. 5 illustrates a concept of one embodiment of the present invention.

FIG. 6 illustrates energy levels of an exciplex applied to one embodiment of the present invention.

FIGS. 7A to 7C each illustrate a light-emitting element of one embodiment of the present invention.

FIG. 8 illustrates a structure of a light-emitting element of Example 2.

FIG. 9 shows voltage-luminance characteristics of the light-emitting element of Example 2.

FIG. 10 shows voltage-current characteristics of the light-emitting element of Example 2.

FIG. 11 shows luminance-power efficiency characteristics of the light-emitting element of Example 2.

FIG. 12 shows luminance-external quantum efficiency characteristics of the light-emitting element of Example 2.

FIG. 13 shows an emission spectrum of the light-emitting element of Example 2.

FIG. 14 shows results of reliability tests of the light-emitting element of Example 2.

FIG. 15 shows a relationship between a peak wavelength of an emission spectrum of an exciplex and a HOMO level of a substance X according to Example 3.

FIG. 16 shows a relationship between a peak wavelength of an emission spectrum of an exciplex and external quantum efficiency of a light-emitting element according to Example 3.

FIG. 17 shows calculation results according to one embodiment of the present invention.

FIGS. 18A1, 18A2, 18B1, 18B2, 18C1, and 18C2 show calculation results according to one embodiment of the present invention.

BEST MODE FOR CARRYING OUT THE INVENTION

Embodiments will be described with reference to drawings. Note that the invention is not limited to the following description, and it will be easily understood by those skilled in the art that various changes and modifications can be made without departing from the spirit and scope of the invention. Therefore, the invention should not be construed as being limited to the description in the following embodiments. Note that in the structures of the invention described below, the same portions or portions having similar functions are denoted by the same reference numerals in different drawings, and description of such portions is not repeated.

Embodiment 1

In this embodiment, a light-emitting element of one embodiment of the present invention will be described.

The light-emitting element of this embodiment includes a light-emitting layer containing a guest material as a light-emitting substance, a first organic compound, and a second organic compound. Specifically, a phosphorescent compound is used as the guest material. Note that one of the first and second organic compounds, the content of which is higher than that of the other in the light-emitting layer, is called host material.

The structure in which the guest material is dispersed in the host material can prevent the light-emitting layer from crystallizing. Further, it is possible to suppress concentration quenching due to high concentration of the guest material, and thus the light-emitting element can have higher emission efficiency.

Note that in this embodiment, it is preferable that a triplet excitation energy level (T₁ level) of each of the first and second organic compounds be higher than that of the guest material. This is because, when the T₁ level of the first organic compound (or the second organic compound) is lower than that of the guest material, the triplet excitation energy of the guest material, which is to contribute to light emission, is quenched by the first organic compound (or the second organic compound) and accordingly the emission efficiency is decreased.

<Elementary Processes of Light Emission>

First, a description is given of general elementary processes of light emission in a light-emitting element using a phosphorescent compound as a guest material.

(1) The case where an electron and a hole are recombined in a guest molecule, and the guest molecule is excited (direct recombination process).

(1-1) When the excited state of the guest molecule is a triplet excited state, the guest molecule emits phosphorescence.

(1-2) When the excited state of the guest molecule is a singlet excited state, the guest molecule in the singlet excited state undergoes intersystem crossing to a triplet excited state and emits phosphorescence.

In other words, in the direct recombination process in (1), as long as the efficiency of intersystem crossing and the phosphorescence quantum yield of the guest molecule are high, high emission efficiency can be obtained. Note that as described above, the T₁ level of the host molecule is preferably higher than the T₁ level of the guest molecule.

(2) The case where an electron and a hole are recombined in a host molecule and the host molecule is put in an excited state (energy transfer process).

(2-1) When the excited state of the host molecule is a triplet excited state and the T₁ level of the host molecule is higher than that of the guest molecule, excitation energy is transferred from the host molecule to the guest molecule, and thus the guest molecule is put in a triplet excited state. The guest molecule in the triplet excited state emits phosphorescence. Note that energy transfer to a singlet excitation energy level (S₁ level) of the guest molecule can occur in theory, but is unlikely to be a main energy transfer process because, in many cases, the S₁ level of the guest molecule has a higher energy than the T₁ level of the host molecule; therefore, a description thereof is not given here.

(2-2) When the excited state of the host molecule is a singlet excited state and the S₁ level of the host molecule is higher than the S₁ level and T₁ level of the guest molecule, excitation energy is transferred from the host molecule to the guest molecule, and thus, the guest molecule is put in a singlet excited state or a triplet excited state. The guest molecule in the triplet excited state emits phosphorescence. In addition, the guest molecule in the singlet excited state undergoes intersystem crossing to a triplet excited state, and emits phosphorescence.

In other words, in the energy transfer process in (2), it is important how efficiently both the triplet excitation energy and the singlet excitation energy of the host molecule can transfer to the guest molecule.

In view of the above-described energy transfer processes, before the excitation energy of the host molecule is transferred to the guest molecule, when the host molecule itself is deactivated by emitting the excitation energy as light or heat, the emission efficiency is decreased. The inventors have found out that when the host molecule is in a singlet excited state (the above (2-2)), the energy is unlikely to transfer to the guest molecule, i.e., the phosphorescent compound, and the emission efficiency is likely to be decreased as compared to when the host molecule is in a triplet excited state (the above (2-1)). Thus, the inventors have focused on that fact as an object. The reason has been found as follows in consideration of a more detailed energy transfer process.

<Energy Transfer Process>

The following describes energy transfer processes between molecules in detail.

First, as a mechanism of energy transfer between molecules, the following two mechanisms are proposed. A molecule providing excitation energy is referred to as host molecule, while a molecule receiving the excitation energy is referred to as guest molecule.

<<Förster Mechanism (Dipole-Dipole Interaction)>>

In Förster mechanism, direct intermolecular contact is not necessary for energy transfer. Through a resonant phenomenon of dipolar oscillation between a host molecule and a guest molecule, energy transfer occurs. By the resonant phenomenon of dipolar oscillation, the host molecule provides energy to the guest molecule, and thus, the host molecule is put in a ground state and the guest molecule is put in an excited state. The rate constant k_(h*→g) of Förster mechanism is expressed by Formula (1).

$\begin{matrix} \left\lbrack {{FORMULA}\mspace{14mu} 1} \right\rbrack & \; \\ {k_{h^{*}->g} = {\frac{9000c^{4}K^{2}\phi\;\ln\; 10}{128\pi^{5}n^{4}N\;\tau\; R^{6}}{\int{\frac{{f_{h}^{\prime}(v)}{ɛ_{g}(v)}}{v^{4}}{dv}}}}} & (1) \end{matrix}$

In Formula (1), v denotes a frequency, f_(h)(v) denotes a normalized emission spectrum of a host molecule (a fluorescent spectrum in energy transfer from a singlet excited state, and a phosphorescent spectrum in energy transfer from a triplet excited state), ε_(g)(v) denotes a molar absorption coefficient of a guest molecule, N denotes Avogadro's number, n denotes a refractive index of a medium, R denotes an intermolecular distance between the host molecule and the guest molecule, τ denotes a measured lifetime of an excited state (fluorescence lifetime or phosphorescence lifetime), c denotes the speed of light, ϕ denotes a luminescence quantum yield (a fluorescence quantum yield in energy transfer from a singlet excited state, and a phosphorescence quantum yield in energy transfer from a triplet excited state), and K² denotes a coefficient (0 to 4) of orientation of a transition dipole moment between the host molecule and the guest molecule. Note that K²=⅔ in random orientation.

<<Dexter Mechanism (Electron Exchange Interaction>>

In Dexter mechanism, a host molecule and a guest molecule are close to a contact effective range where their orbitals overlap, and the host molecule in an excited state and the guest molecule in a ground state exchange their electrons, which leads to energy transfer. The rate constant k_(h*→g) of Dexter mechanism is expressed by Formula (2).

$\begin{matrix} \left\lbrack {{FORMULA}\mspace{14mu} 2} \right\rbrack & \; \\ {k_{h^{*}->g} = {\left( \frac{2\pi}{h} \right)K^{2}{\exp\left( {- \frac{2R}{L}} \right)}{\int{{f_{h}^{\prime}(v)}{ɛ_{g}^{\prime}(v)}{dv}}}}} & (2) \end{matrix}$

In Formula (2), h denotes a Planck constant, K denotes a constant having an energy dimension, v denotes a frequency, f_(h)(v) denotes a normalized emission spectrum of a host molecule (a fluorescent spectrum in energy transfer from a singlet excited state, and a phosphorescent spectrum in energy transfer from a triplet excited state), ε′_(g)(v) denotes a normalized absorption spectrum of a guest molecule, L denotes an effective molecular radius, and R denotes an intermolecular distance between the host molecule and the guest molecule.

Here, the efficiency of energy transfer from the host molecule to the guest molecule (energy transfer efficiency Φ_(ET)) is thought to be expressed by Formula (3). In the formula, k_(r) denotes a rate constant of a light-emission process (fluorescence in energy transfer from a singlet excited state, and phosphorescence in energy transfer from a triplet excited state) of a host molecule, k_(a) denotes a rate constant of a non-light-emission process (thermal deactivation or intersystem crossing) of a host molecule, and τ denotes a measured lifetime of an excited state of a host molecule.

$\begin{matrix} \left\lbrack {{FORMULA}\mspace{14mu} 3} \right\rbrack & \; \\ {\Phi_{ET} = {\frac{k_{h^{*}->g}}{k_{r} + k_{n} + k_{h^{*}->g}} = \frac{k_{h^{*}->g}}{\left( \frac{1}{\tau} \right) + k_{h^{*}->g}}}} & (3) \end{matrix}$

First, according to Formula (3), it is found that the energy transfer efficiency Φ_(ET) can be increased by further increasing the rate constant k_(h*→g) of energy transfer as compared with another competing rate constant k_(r)+k_(n)(=1/τ). Then, in order to increase the rate constant k_(h*→g) of energy transfer, based on Formulae (1) and (2), in Förster mechanism and Dexter mechanism, it is preferable that an emission spectrum of a host molecule (a fluorescent spectrum in energy transfer from a singlet excited state, and a phosphorescent spectrum in energy transfer from a triplet excited state) largely overlap with an absorption spectrum of a guest molecule.

Here, the present inventors have considered that the absorption band on the longest wavelength side (lowest energy side) in the absorption spectrum of the guest molecule is important in considering the overlap between the emission spectrum of the host molecule and the absorption spectrum of the guest molecule.

In this embodiment, a phosphorescent compound is used as the guest material. In an absorption spectrum of the phosphorescent compound, an absorption band that is considered to contribute to light emission most greatly is an absorption wavelength corresponding to direct transition from a singlet ground state to a triplet excitation state and a vicinity of the absorption wavelength, which is on the longest wavelength side. Therefore, it is considered preferable that the emission spectrum (a fluorescent spectrum and a phosphorescent spectrum) of the host material overlap with the absorption band on the longest wavelength side in the absorption spectrum of the phosphorescent compound.

For example, most organometallic complexes, especially light-emitting iridium complexes, have a broad absorption band at around 500 nm to 600 nm as the absorption band on the longest wavelength side (as a matter of fact, the broad absorption band can be on a shorter or longer wavelength side depending on emission wavelengths). This absorption band is mainly based on a triplet MLCT (metal to ligand charge transfer) transition. Note that it is considered that the absorption band also includes absorptions based on a triplet π-π* transition and a singlet MLCT transition, and that these absorptions overlap one another to form a broad absorption band on the longest wavelength side in the absorption spectrum. In other words, it can be considered that the difference between the lowest singlet excited state and the lowest triplet excited state is small, and absorptions based on these states overlap each other to form a broad absorption band on the longest wavelength side in the absorption spectrum. Therefore, as described above, it is preferable that the broad absorption band on the longest wavelength side largely overlap with the emission spectrum of the host material when an organometallic complex (especially iridium complex) is used as the guest material.

Here, first, energy transfer from a host material in a triplet excited state will be considered. From the above-described discussion, it is preferable that, in energy transfer from a triplet excited state, the phosphorescent spectrum of the host material and the absorption band on the longest wavelength side of the guest material largely overlap each other.

Note that a fluorescent compound is generally used as the host material; thus, phosphorescence lifetime (τ) is a millisecond or longer which is extremely long (i.e., k_(r)+k_(n) is low). This is because the transition from the triplet excited state to the ground state (singlet) is a forbidden transition. Formula (3) shows that this is favorable to energy transfer efficiency Φ_(ET). This also suggests that energy is generally likely to be transferred from the host material in the triplet excited state to the guest material in the triplet excited state.

However, a question here is energy transfer from the host material in the singlet excited state. In order to efficiently perform not only energy transfer from the triplet excited state but also energy transfer from the singlet excited state, it is clear from the above-described discussion that the host material needs to be designed so as to have not only its phosphorescent spectrum but also its fluorescent spectrum overlapping with the absorption band on the longest wavelength side of the guest material. In other words, unless the host material is designed so as to have its fluorescent spectrum in a position similar to that of its phosphorescent spectrum, it is not possible to achieve efficient energy transfer from the host material in both the singlet excited state and the triplet excited state.

However, the S₁ level generally differs greatly from the T₁ level (S₁ level >T₁ level); therefore, the fluorescence emission wavelength also differs greatly from the phosphorescence emission wavelength (fluorescence emission wavelength <phosphorescence emission wavelength). For example, 4,4′-di(N-carbazolyl)biphenyl (abbreviation: CBP), which is commonly used as a host material in a light-emitting element including a phosphorescent compound, has a phosphorescent spectrum at around 500 nm and has a fluorescent spectrum at around 400 nm, which are largely different by about 100 nm. This example also shows that it is extremely difficult to design a host material so as to have its fluorescent spectrum in a position similar to that of its phosphorescent spectrum. Therefore, the present inventors consider it a major challenge to improve efficiency in energy transfer from the host material in the singlet excited state to the guest material.

Note that fluorescence lifetime (τ) of a fluorescent compound that is used as the host material is on the order of nanoseconds which is extremely short (i.e., k_(r)+k_(n) is high). This is because the transition from the singlet excited state to the ground state (singlet) is an allowed transition. Formula (3) shows that this is unfavorable to energy transfer efficiency Φ_(ET). This also suggests that energy is generally unlikely to be transferred from the host material in the singlet excited state to the guest material.

One embodiment of the present invention is a useful technique which can overcome such a problem of the efficiency of the energy transfer from the host material in the singlet excited state to the guest material.

Note that it has been considered so far that a light-emitting element including a phosphorescent compound can theoretically achieve an internal quantum efficiency of 100% because intersystem crossing makes it possible to convert both the single excited state and the triplet excited state into light emission (refer to “(1) direct recombination process” described above). In addition, it has been discussed that a light-emitting element having an external quantum efficiency as high as 20% under the assumption that the light extraction efficiency is 20% achieved an internal quantum efficiency of substantially 100%. However, it is considered in fact that these conventional light-emitting elements have not achieved an internal quantum efficiency of 100% because the above-described energy transfer from the singlet excited state of the host material has been overlooked. This is based on the fact that the present inventors have achieved an external quantum efficiency of 27% or more by carrying out one embodiment of the present invention which is described below (see FIG. 12 and Example 2). It can be said that the value is equal to or exceeds a conventional theoretical limit of external quantum efficiency. In other words, an external quantum efficiency of at least 27% or more corresponds to an internal quantum efficiency of 100%, and one embodiment of the present invention is a useful technique for achieving it. Note that this indicates that a conventional external quantum efficiency of 20% can be estimated to correspond to an internal quantum efficiency of 75% or less.

As described above, by application of one embodiment of the present invention, a light-emitting element with high external quantum efficiency can be provided.

One Embodiment of Present Invention

One embodiment of the present invention is a light-emitting element which includes a light-emitting layer containing a phosphorescent compound, a first organic compound, and a second organic compound between a pair of electrodes, in which a combination of the first organic compound and the second organic compound forms an exciplex, in which an emission spectrum of the exciplex overlaps with an absorption band located on the longest wavelength side of an absorption spectrum of the phosphorescent compound, and in which a peak wavelength of the emission spectrum of the exciplex is longer than or equal to a peak wavelength of the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound.

The first organic compound and the second organic compound form an exciplex (also referred to as excited complex) through recombination of carriers (i.e., electrons and holes) (or from a singlet exciton). In the case where the exciplex formed emits light, the emission wavelength thereof is located on the longer wavelength side as compared to the emission wavelength (fluorescent wavelength) of each of the first and second organic compounds. In other words, by formation of the exciplex, the fluorescent spectrum of the first organic compound and the fluorescent spectrum of the second organic compound can be converted into an emission spectrum which is located on the longer wavelength side.

Therefore, as illustrated in FIG. 5, even when the fluorescent spectrum of the first organic compound (or the second organic compound) is located on the shorter wavelength side as compared to the absorption band of the phosphorescent compound which is located on the longest wavelength side, and does not have an overlap with the absorption band, an emission spectrum with a long wavelength can be obtained by forming an exciplex so as to have a large overlap with the absorption band. The light-emitting element of one embodiment of the present invention transfers energy by utilizing the overlap between the emission spectrum of the exciplex and the absorption spectrum of the phosphorescent compound and thus has high energy transfer efficiency. Therefore, in one embodiment of the present invention, a light-emitting element having high external quantum efficiency can be obtained.

In addition, the exciplex exists only in an excited state and thus has no ground state capable of absorbing energy. Therefore, a phenomenon in which the phosphorescent compound is deactivated by reverse energy transfer of the singlet excited state and triplet excited state of the phosphorescent compound to the exciplex before light emission (i.e., emission efficiency is lowered) is not considered to occur in principle. This also contributes to improvement of external quantum efficiency.

In addition, the exciplex is considered to have an extremely small difference between singlet excited energy and triplet excited energy. In other words, the emission spectrum of the exciplex from the singlet state and the emission spectrum thereof from the triplet state are highly close to each other. Accordingly, in the case where a design is implemented such that the emission spectrum of the exciplex (generally the emission spectrum of the exciplex from the singlet state) overlaps with the absorption band of the phosphorescent compound on the longest wavelength side as described above, the emission spectrum of the exciplex from the triplet state (which is not observed at room temperature and not observed even at low temperature in many cases) also overlaps with the absorption band of the phosphorescent compound which is located on the longest wavelength side. More specifically, this means that energy can be efficiently transferred to the phosphorescent compound from the exciplex in both the singlet state and the triplet state.

Molecular orbital calculations were performed as described below to verify whether or not an exciplex actually has such characteristics. In general, a combination of a heteroaromatic compound and an aromatic amine often forms an exciplex under the influence of the lowest unoccupied molecular orbital (LUMO) level of the heteroaromatic compound which is deeper than the LUMO level of the aromatic amine (the property of easily accepting electrons) and the highest occupied molecular orbital (HOMO) level of the aromatic amine which is shallower than the HOMO level of the heteroaromatic compound (the property of easily accepting holes). Thus, calculations were performed using a combination of dibenzo[f,h]quinoxaline (abbreviation: DBq) which is a typical skeleton forming the LUMO of a heteroaromatic compound and triphenylamine (abbreviation: TPA) which is a typical skeleton forming the HOMO of an aromatic amine.

First, the optimal molecular structures and the excitation energies of DBq alone and TPA alone in the lowest singlet excited state (S₁) and the lowest triplet excited state (T₁) were calculated using the time-dependent density functional theory (TD-DFT). Furthermore, the excitation energy of a dimer of DBq and TPA was also calculated. In the DFT, the total energy is represented as the sum of potential energy, electrostatic energy between electrons, electronic kinetic energy, and exchange-correlation energy including all the complicated interactions between electrons. Also in the DFT, an exchange-correlation interaction is approximated by a functional (a function of another function) of one electron potential represented in terms of electron density to enable high-speed, high-accuracy calculations. Here, B3LYP which was a hybrid functional was used to specify the weight of each parameter related to exchange-correlation energy. In addition, as a basis function, 6-311 (a basis function of a triple-split valence basis set using three contraction functions for each valence orbital) was applied to all the atoms. By the above basis function, for example, 1s to 3s orbitals are considered in the case of hydrogen atoms, while 1s to 4s and 2p to 4p orbitals are considered in the case of carbon atoms. Furthermore, to improve calculation accuracy, the p function and the d function as polarization basis sets were added to hydrogen atoms and atoms other than hydrogen atoms, respectively.

Note that Gaussian 09 was used as a quantum chemistry computational program. A high performance computer (Altix 4700, manufactured by SGI Japan, Ltd.) was used for the calculations.

First, the HOMO levels and the LUMO levels of DBq alone, TPA alone, and a dimer of DBq and TPA were calculated. FIG. 17 shows the HOMO levels and the LUMO levels, and FIGS. 18A1, 18A2, 18B1, 18B2, 18C1, and 18C2 show HOMO and LUMO distributions.

FIG. 18A1 shows the LUMO distribution of DBq alone; FIG. 18A2, the HOMO distribution of DBq alone; FIG. 18B1, the LUMO distribution of TPA alone; FIG. 18B2, the HOMO distribution of TPA alone; FIG. 18C1, the LUMO distribution of the dimer of DBq and TPA; and FIG. 18C2, the HOMO distribution of the dimer of DBq and TPA.

As shown in FIG. 17, it is suggested that the dimer of DBq and TPA forms an exciplex of DBq and TPA under the influence of the LUMO level (−1.99 eV) of DBq which is deeper (lower) than the LUMO level of TPA and the HOMO level (−5.21 eV) of TPA which is shallower (higher) than the HOMO level of DBq. In fact, as is clear from FIGS. 18C1 and 18C2, the LUMO of the dimer of DBq and TPA is distributed on the DBq side, and the HOMO thereof is distributed on the TPA side.

Next, excitation energies obtained from the optimal molecular structures of DBq alone in S₁ and T₁ will be shown. Here, the S₁ and T₁ excitation energies correspond to fluorescence and phosphorescence wavelengths, respectively, obtained from DBq alone. The S₁ excitation energy of DBq alone is 3.294 eV, and the fluorescence wavelength is 376.4 nm. The T₁ excitation energy of DBq alone is 2.460 eV, and the phosphorescence wavelength is 504.1 nm.

In addition, excitation energies obtained from the optimal molecular structures of TPA alone in S₁ and T₁ will be shown. Here, the S₁ and T₁ excitation energies correspond to fluorescence and phosphorescence wavelengths, respectively, obtained from TPA alone. The S₁ excitation energy of TPA alone is 3.508 eV, and the fluorescence wavelength is 353.4 nm. The T₁ excitation energy of TPA alone is 2.610 eV, and the phosphorescence wavelength is 474.7 nm.

Furthermore, excitation energies obtained from the optimal molecular structures of the dimer of DBq and TPA in S₁ and T₁ will be shown. The S₁ and T₁ excitation energies correspond to fluorescence and phosphorescence wavelengths, respectively, obtained from the dimer of DBq and TPA. The S₁ excitation energy of the dimer of DBq and TPA is 2.036 eV, and the fluorescence wavelength is 609.1 nm. The T₁ excitation energy of the dimer of DBq and TPA is 2.030 eV, and the phosphorescence wavelength is 610.0 nm.

It is found from the above that each of the phosphorescence wavelengths of DBq alone and TPA alone is shifted to the longer wavelength side by about 100 nm as compared to the fluorescence wavelength. This result shows a tendency similar to that of CBP (measured values) described above and supports the validity of the calculations.

On the other band, it is found that the fluorescence wavelength of the dimer of DBq and TPA is located on the longer wavelength side as compared to the fluorescence wavelengths of DBq alone and TPA alone. This result shows a tendency similar to that of examples (measured values) described below and supports the validity of the calculations. It is also found that the difference between the fluorescence wavelength and the phosphorescence wavelength of the dimer of DBq and TPA is only 0.9 nm and that these wavelengths are substantially the same.

These results indicate that the exciplex can integrate the singlet excitation energy and the triplet excitation energy into substantially the same energy. Therefore, it is indicated as described above that the exciplex can efficiently transfer energy to the phosphorescent compound from both the singlet state and the triplet state thereof.

Such an effect is specific to the use of an exciplex as a medium for energy transfer. In general, energy transfer from the singlet excited state or triplet excited state of a host material to a phosphorescent compound is considered. On the other hand, one embodiment of the present invention greatly differs from a conventional technique in that an exciplex of a host material and another material (an exciplex of a first organic compound and a second organic compound) is formed first and energy transfer from the exciplex is used. In addition, this difference provides unprecedentedly high emission efficiency.

Note that in general, the use of an exciplex for a light-emitting layer of a light-emitting element has a value such as being capable of controlling the emission color, but usually causes a significant decrease in emission efficiency. Therefore, the use of an exciplex has been considered unsuitable for obtaining a highly efficient light-emitting element. However, the present inventors have found that the use of an exciplex as a medium for energy transfer to a phosphorescent compound enables, on the contrary, emission efficiency to be maximized as shown in one embodiment of the present invention. This technical idea conflicts with the conventional fixed idea.

Further, in the light-emitting element of one embodiment of the present invention, the threshold value of voltage with which an exciplex is formed through carrier recombination (or from a singlet exciton) depends on the energy of a peak of the emission spectrum of the exciplex. When the emission spectrum of the exciplex peaks at 620 nm (2.0 eV), for example, the threshold value of voltage that is needed when the exciplex is formed with electric energy is also approximately 2.0 V.

Here, when the energy of the peak of the emission spectrum of the exciplex is too high (i.e., when the wavelength is too short), the threshold value of the voltage with which an exciplex is formed also increases. That case is not preferred because higher voltage is needed to make the phosphorescent compound emit light by energy transfer from the exciplex to the phosphorescent compound, and thus extra energy is consumed.

In view of this, it is preferable that energy of the peak of the emission spectrum of the exciplex be lower (the wavelength be longer) because in that case, the threshold value of the voltage is smaller. Accordingly, the light-emitting element of one embodiment of the present invention, in which the peak wavelength of the emission spectrum of the exciplex is longer than or equal to the peak wavelength of the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound, can be driven at low drive voltage. In addition, in the light-emitting element of one embodiment of the present invention, even when the peak wavelength of the emission spectrum of the exciplex is longer than or equal to the peak wavelength of the absorption spectrum of the phosphorescent compound, energy can be transferred utilizing the overlap between the emission spectrum of the exciplex and the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound, which leads to high emission efficiency of the light-emitting element. As described above, high emission efficiency (external quantum efficiency) is obtained with the drive voltage reduced, whereby high power efficiency can be achieved.

In the above-described light-emitting element, since the peak wavelength of the emission spectrum of the exciplex is particularly long, the drive voltage can be lower. This can be explained as follows.

One embodiment of the present invention includes a light-emitting element in which the peak wavelength of the emission spectrum of the exciplex is longer than or equal to the peak wavelength of the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound (i.e., the energy of the emission peak of the exciplex is lower than or equal to the energy of the absorption peak of the phosphorescent compound). Therefore, in the light-emitting element, a value of voltage with which an exciplex is formed through carrier recombination is smaller than a value of voltage with which the phosphorescent compound starts to emit light by carrier recombination.

In other words, even when voltage that has a value smaller than that of voltage with which the phosphorescent compound starts to emit light is applied to the light-emitting element, carrier recombination occurs and an exciplex is formed; thus, recombination current starts to flow in the light-emitting element. Therefore, a light-emitting element with lower drive voltage (with more favorable voltage-current characteristics) can be provided.

Accordingly, at the time when the voltage reaches a value with which the phosphorescent compound starts to emit light, a sufficient number of carriers exist in the light-emitting layer and carrier recombination which can contribute to light emission of the phosphorescent compound smoothly occurs many times. Therefore, luminance becomes remarkably high at a voltage close to the threshold voltage (emission start voltage) of the phosphorescent compound. In other words, a curve representing the voltage-luminance characteristics can be steep in a rising portion near the emission start voltage; thus, drive voltage needed to obtain desired luminance can be low. Further, to obtain practical luminance, driving is performed with voltage higher than or equal to the threshold voltage (emission start voltage) of the phosphorescent compound, in which case emitted light originates mostly from the phosphorescent compound and the light-emitting element is thus allowed to have high current efficiency.

Note that the phosphorescent compound used in one embodiment of the present invention has a singlet absorption spectrum and a triplet absorption spectrum which are located close to each other. Moreover, in an exciplex formed in one embodiment of the present invention, a peak of an emission spectrum of the exciplex from the singlet state and a peak of an emission spectrum of the exciplex from the triplet state can be considered to be located close to each other. Therefore, even when the peak of the emission spectrum of the exciplex (usually the emission spectrum of the exciplex from the singlet state) is located close to the peak of the emission spectrum of the phosphorescent compound, quenching of triplet excitation energy of the phosphorescent compound due to the exciplex in the triplet state can be suppressed. In the first place, the exciplex does not have an absorption spectrum; thus, a phenomenon is less likely to occur in which the triplet excitation energy of the phosphorescent compound transfers to the exciplex to be quenched. This also suggests that the light-emitting element of one embodiment of the present invention has high external quantum efficiency. The above also is an advantage of using an exciplex.

One embodiment of the present invention is a light-emitting element which includes a light-emitting layer containing a phosphorescent compound, a first organic compound, and a second organic compound between a pair of electrodes, in which a combination of the first organic compound and the second organic compound forms an exciplex, in which an emission spectrum of the exciplex overlaps with an absorption band located on the longest wavelength side of an absorption spectrum of the phosphorescent compound, and in which a difference between a peak wavelength of the emission spectrum of the exciplex and a peak wavelength of an emission spectrum of the phosphorescent compound is 30 nm or less.

The light-emitting element can be driven at low drive voltage and have sufficiently high emission efficiency when the peak of the emission spectrum of the exciplex (usually the emission spectrum of the exciplex from the singlet state) is located close to the peak of the emission spectrum of the phosphorescent compound as described above. The effect of a reduction in drive voltage is enhanced especially when the peak of the emission spectrum of the exciplex is located in a region ranging from the peak of the emission spectrum of the phosphorescent compound to a wavelength 30 nm longer than the peak of the emission spectrum of the phosphorescent compound. Further, relatively high emission efficiency can be maintained when the peak of the emission spectrum of the exciplex is in a region ranging from the peak of the emission spectrum of the phosphorescent compound to a wavelength 30 nm shorter than the peak of the emission spectrum of the phosphorescent compound.

However, when the peak of the emission spectrum of the exciplex is located on the longer wavelength side as compared to the peak of the emission spectrum of the phosphorescent compound, the external quantum efficiency of the light-emitting element is reduced in some cases. The reason for this is that under this condition, the overlap between the emission spectrum of the exciplex and the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound is decreased, excitation energy transfer from the exciplex to the phosphorescent compound is thus unlikely to occur, and the exciplex itself is easily deactivated by emitting the excitation energy as light or heat.

Thus, for achievement of extremely high emission efficiency, another embodiment of the present invention is a light-emitting element which includes a light-emitting layer containing a phosphorescent compound, a first organic compound, and a second organic compound between a pair of electrodes, in which a combination of the first organic compound and the second organic compound forms an exciplex, in which an emission spectrum of the exciplex overlaps with an absorption band located on the longest wavelength side of an absorption spectrum of the phosphorescent compound, and in which a peak wavelength of the emission spectrum of the exciplex is longer than or equal to a peak wavelength of the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound and shorter than or equal to a peak wavelength of an emission spectrum of the phosphorescent compound.

In the light-emitting element, the peak wavelength of the emission spectrum of the exciplex is shorter than or equal to the peak wavelength of the emission spectrum of the phosphorescent compound, and thus the overlap between the emission spectrum of the exciplex and the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound is increased. Therefore, excitation energy can be efficiently transferred from the exciplex to the phosphorescent compound. Accordingly, energy deactivation can be suppressed. Accordingly, a light-emitting element having low drive voltage and high external quantum efficiency can be obtained.

Specifically, it is preferable that a difference between the peak wavelength of the emission spectrum of the exciplex and the peak wavelength of the emission spectrum of the phosphorescent compound be 30 nm or less.

In addition, in one embodiment of the present invention, an exciplex is formed from a singlet exciton of the first organic compound or the second organic compound.

In a light-emitting element of one embodiment of the present invention, a possible elementary process of formation of an exciplex is that one of the first and second organic compounds forms a singlet exciton and then interacts with the other in the ground state. As described above, the emission spectrum of the exciplex and the absorption spectrum of the phosphorescent compound can largely overlap; thus, energy transfer efficiency can be increased. Accordingly, a light-emitting element having high external quantum efficiency can be obtained.

The singlet exciton has a short excitation lifetime (small t) as described above. Thus, there is a problem in that part of excitation energy is deactivated (through light emission or thermal deactivation) before the excitation energy is transferred from the singlet exciton to a guest material (Φ_(ET) tends to be small in Formula (3)). However, in one embodiment of the present invention, such deactivation of excitation energy can be suppressed because the singlet exciton rapidly forms an exciplex. Furthermore, the exciplex has a relatively long excitation lifetime, which is considered favorable to energy transfer efficiency Φ_(ET). Accordingly, the deactivation of the singlet excitation energy of the host material that may affect not only the efficiency of an element but also the lifetime thereof can be suppressed by application of one embodiment of the present invention, so that a light-emitting element having a long lifetime can be obtained.

In one embodiment of the present invention, it is also preferable that the excitation energy of the exciplex be sufficiently transferred to the phosphorescent compound, and that light emission from the exciplex be not substantially observed. Therefore, energy is preferably transferred to the phosphorescent compound through the exciplex so that the phosphorescent compound emits phosphorescence.

According to the above-described concept of energy transfer, one embodiment of the present invention is effective in the case where at least one of the first and second organic compounds is a fluorescent compound (i.e., a compound which is likely to undergo light emission or thermal deactivation from the singlet excited state). Therefore, it is preferable that at least one of the first and second organic compounds be a fluorescent compound.

Note that in the case where a phosphorescent compound is used as an organic compound serving as a host material, the organic compound itself is likely to emit light and unlikely to allow energy to be transferred to a guest material. In this case, it is favorable if the organic compound could emit light efficiently, but it is difficult to achieve high emission efficiency because the organic compound serving as a host material causes the problem of concentration quenching. For this reason, it is preferable that the organic compound be a fluorescent compound and energy transfer be achieved with the above-described composition.

In addition, in one embodiment of the present invention, it is preferable that the phosphorescent compound be an organometallic complex.

The exciplex used in one embodiment of the present invention will be described in detail below.

<Exciplex>

The exciplex (excited complex) is formed by an interaction between dissimilar molecules in excited states. The exciplex is generally known to be easily formed between a material having a relatively deep LUMO level and a material having a relatively shallow HOMO level.

An emission wavelength depends on a difference in energy between the HOMO level and the LUMO level. When the energy difference is large, the emission wavelength is short. When the energy difference is small, the emission wavelength is long.

Here, the HOMO levels and LUMO levels of the first organic compound and the second organic compound used in one embodiment of the present invention are different from each other. Specifically, the energy levels are higher in the following order: the HOMO level of the first organic compound <the HOMO level of the second organic compound <the LUMO level of the first organic compound <the LUMO level of the second organic compound (see FIG. 6).

When the exciplex is formed by these two organic compounds, the LUMO level and the HOMO level of the exciplex originate from the first organic compound and the second organic compound, respectively (see FIG. 6). Therefore, the energy difference of the exciplex is smaller than the energy difference of the first organic compound and the energy difference of the second organic compound. In other words, the emission wavelength of the exciplex is longer than the emission wavelengths of the first organic compound and the second organic compound.

The formation process of the exciplex used in one embodiment of the present invention is considered to be roughly classified into two processes.

<<Electroplex>>

In this specification, the term “electroplex” means that the first organic compound in the ground state and the second organic compound in the ground state directly form an exciplex.

As described above, in general, when an electron and a hole are recombined in a host material, excitation energy is transferred from the host material in an excited state to a guest material, whereby the guest material is brought into an excited state to emit light.

At this time, before the excitation energy is transferred from the host material to the guest material, the host material itself emits light or the excitation energy turns into thermal energy, which leads to partial deactivation of the excitation energy. In particular, when the host material is in a singlet excited state, excitation lifetime is shorter than that when it is in a triplet excited state, which easily leads to deactivation of singlet excitation energy. The deactivation of excitation energy is one of causes for a decrease in lifetime of a light-emitting element.

However, in one embodiment of the present invention, an electroplex is formed from the first organic compound and the second organic compound having carriers (cation or anion); therefore, formation of a singlet exciton having a short excitation lifetime can be suppressed. In other words, there can be a process where an exciplex is directly formed without formation of a singlet exciton. Thus, deactivation of the singlet excitation energy can be inhibited. Accordingly, a light-emitting element having a long lifetime can be obtained.

For example, in the case where the first organic compound is a compound having an electron-trapping property and the second organic compound is a compound having a hole-trapping property, an electroplex is formed directly from an anion of the first organic compound and a cation of the second organic compound. It is a novel concept to obtain a light-emitting element having high emission efficiency by suppressing the generation of the singlet excited state of a host material and transferring energy from an electroplex to a guest material, in the above-described manner. Note that the generation of the triplet excited state of the host material is similarly suppressed and an electroplex is directly formed; therefore, energy transfer is considered to occur from the electroplex to the guest material. This mechanism is also novel.

The emission spectrum of the electroplex formed is located on the longer wavelength side as compared to the emission wavelength of each of the first and second organic compounds.

The overlap between the emission spectrum of the electroplex and the absorption spectrum of the phosphorescent compound is larger than the overlap between the emission spectrum of the first organic compound (or the second organic compound) and the absorption spectrum of the phosphorescent compound. The light-emitting element of one embodiment of the present invention transfers energy by utilizing the overlap between the emission spectrum of the electroplex and the absorption spectrum of the phosphorescent compound and thus has high energy transfer efficiency. Therefore, in one embodiment of the present invention, a light-emitting element having high external quantum efficiency can be obtained.

<<Formation of Exciplex by Exciton>>

As another process, there is thought to be an elementary process where one of the first and second organic compounds forms a singlet exciton and then interacts with the other in the ground state to form an exciplex. Unlike an electroplex, a singlet excited state of the first organic compound or the second organic compound is temporarily generated in this case, but this is rapidly converted into an exciplex, and thus, deactivation of single excitation energy can be inhibited. Thus, it is possible to inhibit deactivation of excitation energy of the first organic compound or the second organic compound. Accordingly, in one embodiment of the present invention, a light-emitting element having a long lifetime can be obtained. Note that it is considered that the triplet excited state of the host material is also rapidly converted into an exciplex and energy is transferred from the exciplex to the guest material.

The emission spectrum of the exciplex formed is located on the longer wavelength side as compared to the emission wavelength of each of the first and second organic compounds.

The overlap between the emission spectrum of the exciplex and the absorption spectrum of the phosphorescent compound is larger than the overlap between the emission spectrum of the first organic compound (or the second organic compound) and the absorption spectrum of the phosphorescent compound. The light-emitting element of one embodiment of the present invention transfers energy by utilizing the overlap between the emission spectrum of the exciplex and the absorption spectrum of the phosphorescent compound and thus has high energy transfer efficiency. Accordingly, in one embodiment of the present invention, a light-emitting element having high external quantum efficiency can be obtained.

For example, in the case where the first organic compound is a compound having an electron-trapping property, the second organic compound is a compound having a hole-trapping property, and the difference between the HOMO levels and the difference between the LUMO levels of these compounds are large (specifically, 0.3 eV or more), electrons are selectively injected into the first organic compound and holes are selectively injected into the second organic compound. In this case, it is thought that the process where an electroplex is formed takes precedence over the process where an exciplex is formed through a singlet exciton.

Note that this embodiment can be combined with any of the other embodiments as appropriate.

Embodiment 2

In this embodiment, a light-emitting element of one embodiment of the present invention will be described with reference to FIGS. 7A to 7C.

FIG. 7A illustrates a light-emitting element including an EL layer 102 between a first electrode 103 and a second electrode 108. The light-emitting element in FIG. 7A includes a hole-injection layer 701, a hole-transport layer 702, a light-emitting layer 703, an electron-transport layer 704, and an electron-injection layer 705 which are stacked over the first electrode 103 in this order, and the second electrode 108 provided thereover.

The first electrode 103 is preferably formed using any of metals, alloys, conductive compounds, mixtures thereof, and the like which have a high work function (specifically, 4.0 eV or more). Specific examples include indium oxide-tin oxide (ITO: indium tin oxide), indium oxide-tin oxide containing silicon or silicon oxide, indium oxide-zinc oxide (indium zinc oxide), indium oxide containing tungsten oxide and zinc oxide (IWZO), and the like. Films of these conductive metal oxides are usually formed by a sputtering method, but may be formed by application of a sol-gel method or the like. For example, an indium oxide-zinc oxide film can be formed by a sputtering method using a target in which zinc oxide is added to indium oxide at 1 wt % to 20 wt %. Further, an IWZO film can be formed by a sputtering method using a target in which tungsten oxide is added to indium oxide at 0.5 wt % to 5 wt % and zinc oxide is added to indium oxide at 0.1 wt % to 1 wt %. Other examples are graphene, gold, platinum, nickel, tungsten, chromium, molybdenum, iron, cobalt, copper, palladium, nitrides of metal materials (e.g., titanium nitride), and the like.

Note that when a layer included in the EL layer 102 and formed in contact with the first electrode 103 is formed using a later-described composite material formed by combining an organic compound and an electron acceptor (an acceptor), as a substance used for the first electrode 103, any of a variety of metals, alloys, electrically conductive compounds, mixtures thereof, and the like can be used regardless of the work function; for example, aluminum, silver, an alloy containing aluminum (e.g., Al—Si), or the like can also be used.

The first electrode 103 can be formed by, for example, a sputtering method, an evaporation method (including a vacuum evaporation method), or the like.

The second electrode 108 is preferably formed using any of metals, alloys, electrically conductive compounds, mixtures thereof and the like which have a low work function (preferably, 3.8 eV or lower). Specific examples thereof include elements that belong to Groups 1 and 2 in the periodic table, that is, alkali metals such as lithium and cesium, alkaline earth metals such as calcium and strontium, magnesium, alloys thereof (e.g., Mg—Ag and Al—Li), rare-earth metals such as europium and ytterbium, alloys thereof, aluminum, silver, and the like.

When a layer included in the EL layer 102 and formed in contact with the second electrode 108 is formed using a later-described composite material formed by combining an organic compound and an electron donor (a donor), any of a variety of conductive materials, such as Al, Ag, ITO, and indium oxide-tin oxide containing silicon or silicon oxide, can be used regardless of the work function.

Note that when the second electrode 108 is formed, a vacuum evaporation method or a sputtering method can be used. In the case of using a silver paste or the like, a coating method, an inkjet method, or the like can be used.

The EL layer 102 includes at least the light-emitting layer 703. For part of the EL layer 102, a known substance can be used, and either a low molecular compound or a high molecular compound can be used. Note that substances forming the EL layer 102 may consist of organic compounds or may include an inorganic compound as a part.

Further, as illustrated in FIG. 7A, the EL layer 102 includes not only the light-emitting layer 703 but also an appropriate combination of the following layers: the hole-injection layer 701 including a substance having a high hole-injection property, the hole-transport layer 702 including a substance having a high hole-transport property, the electron-transport layer 704 including a substance having a high electron-transport property, the electron-injection layer 705 including a substance having a high electron-injection property, and the like.

The hole-injection layer 701 is a layer that contains a substance having a high hole-injection property. As the substance having a high hole-injection property, a metal oxide such as molybdenum oxide, titanium oxide, vanadium oxide, rhenium oxide, ruthenium oxide, chromium oxide, zirconium oxide, hafnium oxide, tantalum oxide, silver oxide, tungsten oxide, or manganese oxide can be used. Alternatively, a phthalocyanine-based compound such as phthalocyanine (abbreviation: H₂Pc) or copper(II) phthalocyanine (abbreviation: CuPc) can be used.

Other examples of the substance which can be used are aromatic amine compounds and the like which are low molecular organic compounds, such as 4,4′,4″-tris(N,N-diphenylamino)triphenylamine (abbreviation: TDATA), 4,4′,4″-tris[N-(3-methylphenyl)-N-phenylamino]triphenylamine (abbreviation: MTDATA), 4,4′-bis[N-(4-diphenylaminophenyl)-N-phenylamino]biphenyl (abbreviation: DPAB), 4,4′-bis(N-{4-[N′-(3-methylphenyl)-N-phenylamino]phenyl}-N-phenylamino)biphenyl (abbreviation: DNTPD), 1,3,5-tris[N-(4-diphenylaminophenyl)-N-phenylamino]benzene (abbreviation: DPA3B), 3-[N-(9-phenylcarbazol-3-yl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzPCA1), 3,6-bis[N-(9-phenylcarbazol-3-yl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzPCA2), and 3-[N-(1-naphthyl)-N-(9-phenylcarbazol-3-yl)amino]-9-phenylcarbazole (abbreviation: PCzPCN1).

Still other examples of the substance which can be used are high molecular compounds (e.g., oligomers, dendrimers, and polymers), such as poly(N-vinylcarbazole) (abbreviation: PVK), poly(4-vinyltriphenylamine) (abbreviation: PVTPA), poly[N-(4-{N′-[4-(4-diphenylamino)phenyl]phenyl-N-phenylamino}phenyl)methacrylamide] (abbreviation: PTPDMA), and poly[N,N-bis(4-butylphenyl)-N,N′-bis(phenyl)benzidine] (abbreviation: Poly-TPD), and high molecular compounds to which acid is added, such as poly(3,4-ethylenedioxythiophene)/poly(styrenesulfonic acid) (PEDOT/PSS), and polyaniline/poly(styrenesulfonic acid) (PAni/PSS).

For the hole-injection layer 701, the composite material formed by combining an organic compound and an electron acceptor (an acceptor) may be used. Such a composite material, in which holes are generated in the organic compound by the electron acceptor, has high hole-injection and hole-transport properties. In this case, the organic compound is preferably a material excellent in transporting the generated holes (a substance having a high hole-transport property).

Examples of the organic compound used for the composite material can be a variety of compounds, such as aromatic amine compounds, carbazole derivatives, aromatic hydrocarbons, and high molecular compounds (e.g., oligomers, dendrimers, and polymers). The organic compound used for the composite material is preferably an organic compound having a high hole-transport property, and is specifically preferably a substance having a hole mobility of 10⁻⁶ cm²/Vs or more. Note that other than these substances, any substance that has a property of transporting more holes than electrons may be used. Organic compounds that can be used for the composite material will be specifically described below.

Examples of the organic compound that can be used for the composite material are aromatic amine compounds, such as TDATA, MTDATA, DPAB, DNTPD, DPA3B, PCzPCA1, PCzPCA2, PCzPCN1, 4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (abbreviation: NPB or α-NPD), N,N′-bis(3-methylphenyl)-N,N′-diphenyl-[1,1′-biphenyl]-4,4′-diamine (abbreviation: TPD), and 4-phenyl-4′-(9-phenylfluoren-9-yl)triphenylamine (abbreviation: BPAFLP), and carbazole derivatives, such as 4,4′-di(N-carbazolyl)biphenyl (abbreviation: CBP), 1,3,5-tris[4-(N-carbazolyl)phenyl]benzene (abbreviation: TCPB), 9-[4-(N-carbazolyl)]phenyl-10-phenylanthracene (abbreviation: CzPA), 9-phenyl-3-[4-(10-phenyl-9-anthryl)phenyl]-9H-carbazole (abbreviation: PCzPA), and 1,4-bis[4-(N-carbazolyl)phenyl]-2,3,5,6-tetraphenylbenzene.

Other examples of the organic compound that can be used are aromatic hydrocarbon compounds, such as 2-tert-butyl-9,10-di(2-naphthyl)anthracene (abbreviation: t-BuDNA), 2-tert-butyl-9,10-di(1-naphthyl)anthracene, 9,10-bis(3,5-diphenylphenyl)anthracene (abbreviation: DPPA), 2-tert-butyl-9,10-bis(4-phenylphenyl)anthracene (abbreviation: t-BuDBA), 9,10-di(2-naphthyl)anthracene (abbreviation: DNA), 9,10-diphenylanthracene (abbreviation: DPAnth), 2-tert-butylanthracene (abbreviation: t-BuAnth), 9,10-bis(4-methyl-1-naphtyl)anthracene (abbreviation: DMNA), 9,10-bis[2-(1-naphthyl)phenyl]-2-tert-butylanthracene, 9,10-bis[2-(1-naphthyl)phenyl]anthracene, and 2,3,6,7-tetramethyl-9,10-di(1-naphthyl)anthracene.

Other examples of the organic compound that can be used are aromatic hydrocarbon compounds, such as 2,3,6,7-tetramethyl-9,10-di(2-naphthyl)anthracene, 9,9′-bianthryl, 10,10′-diphenyl-9,9′-bianthryl, 10,10′-bis(2-phenylphenyl)-9,9′-bianthryl, 10,10′-bis[(2,3,4,5,6-pentaphenyl)phenyl]-9,9′-bianthryl, anthracene, tetracene, rubrene, perylene, 2,5,8,11-tetra(tert-butyl)perylene, pentacene, coronene, 4,4′-bis(2,2-diphenylvinyl)biphenyl (abbreviation: DPVBi), and 9,10-bis[4-(2,2-diphenylvinyl)phenyl]anthracene (abbreviation: DPVPA).

Further, examples of the electron acceptor are organic compounds, such as 7,7,8,8-tetracyano-2,3,5,6-tetrafluoroquinodimethane (abbreviation: F₄-TCNQ) and chloranil, oxides of transition metals, oxides of metals that belong to Groups 4 to 8 in the periodic table, and the like. Specifically, vanadium oxide, niobium oxide, tantalum oxide, chromium oxide, molybdenum oxide, tungsten oxide, manganese oxide, and rhenium oxide are preferable because of their high electron-accepting property. Among these, molybdenum oxide is especially preferable since it is stable in the air, has a low hygroscopic property, and is easy to handle.

The composite material may be formed using the above-described electron acceptor and the above-described high molecular compound such as PVK, PVTPA, PTPDMA, or Poly-TPD, and may be used for the hole-injection layer 701.

The hole-transport layer 702 is a layer that contains a substance having a high hole-transport property. Examples of the substance having a high hole-transport property are aromatic amine compounds such as NPB, TPD, BPAFLP, 4,4′-bis[N-(9,9-dimethylfluoren-2-yl)-N-phenylamino]biphenyl (abbreviation: DFLDPBi), and 4,4′-bis[N-(spiro-9,9′-bifluoren-2-yl)-N-phenylamino]biphenyl (abbreviation: BSPB). The substances mentioned here are mainly substances that have a hole mobility of 10⁻⁶ cm²/Vs or more. Note that other than these substances, any substance that has a property of transporting more holes than electrons may be used. Note that the layer containing a substance having a high hole-transport property is not limited to a single layer, and may be a stack of two or more layers containing any of the above substances.

For the hole-transport layer 702, a carbazole derivative such as CBP, CzPA, or PCzPA or an anthracene derivative such as t-BuDNA, DNA, or DPAnth may be used.

For the hole-transport layer 702, a high molecular compound such as PVK, PVTPA, PTPDMA, or Poly-TPD can also be used.

The light-emitting layer 703 is a layer that contains a light-emitting substance. The light-emitting layer 703 of this embodiment contains a phosphorescent compound, a first organic compound, and a second organic compound. The phosphorescent compound is a light-emitting substance (guest material). One of the first and second organic compounds, the content of which is higher than that of the other in the light-emitting layer 703, is a host material. Embodiment 1 can be referred to for specifics.

As the phosphorescent compound, an organometallic complex is preferable, and in particular, an iridium complex is preferable. In consideration of energy transfer due to Förster mechanism described above, the molar absorption coefficient of the absorption band of the phosphorescent compound which is located on the longest wavelength side is preferably 2000 M⁻¹ cm⁻¹ or more, more preferably 5000 M⁻¹·cm⁻¹ or more. Examples of the compound having such a high molar absorption coefficient are bis(3,5-dimethyl-2-phenylpyrazinato)(dipivaloylmethanato)iridium(III) (abbreviation: [Ir(mppr-Me)₂(dpm)]), (acetylacetonato)bis(4,6-diphenylpyrimidinato)iridium(III) (abbreviation: [Ir(dppm)₂(acac)]), and the like.

For the first organic compound and the second organic compound, a combination of a compound which is likely to accept electrons (a compound having an electron-trapping property) and a compound which is likely to accept holes (a compound having a hole-trapping property) is preferably employed. With such a composition, it is possible to obtain the effect of improvement of emission efficiency and lifetime not only by energy transfer from an exciplex but also by adjustment of carrier balance between hole transport and electron transport in a light-emitting layer.

As a typical example of a compound which is likely to accept electrons, heteroaromatic compounds can be given. For example, the following can be given: 2-[3-(dibenzothiophen-4-yl)phenyl]dibenzo[f,h]quinoxaline (abbreviation: 2mDBTPDBq-II), 2-[4-(3,6-diphenyl-9H-carbazol-9-yl)pheny]dibenzo[f,h]quinoxaline (abbreviation: 2CzPDBq-III), 7-[3-(dibenzothiophen-4-yl)phenyl]dibenzo[f,h]quinoxaline (abbreviation: 7mDBTPDBq-II), and 6-[3-(dibenzothiophen-4-yl)phenyl]dibenzo[f,h]quinoxaline (abbreviation: 6mDBTPDBq-II).

As typical examples of a compound which is likely to accept holes, aromatic amine compounds and carbazole compounds can be given. For example, the following can be given: 4-phenyl-4′-(9-phenyl-9H-carbazol-3-yl)triphenylamine (abbreviation: PCBA1BP), 3-[N-(1-naphthyl)-N-(9-phenylcarbazol-3-yl)amino]-9-phenylcarbazole (abbreviation: PCzPCN1), 4,4′,4″-tris[N-(1-naphthyl)-N-phenylamino]triphenylamine (abbreviation: 1′-TNATA or 1-TNATA), 2,7-bis[N-(4-diphenylaminophenyl)-N-phenylamino]-spiro-9,9′-bifluorene (abbreviation: DPA2SF), N,N-bis(9-phenylcarbazol-3-yl)-N,N-diphenylbenzene-1,3-diamine (abbreviation: PCA2B), N-(9,9-dimethyl-2-N′,N′-diphenylamino-9H-fluoren-7-yl)diphenylamine (abbreviation: DPNF), N,N′,N″-triphenyl-N,N′,N″-tris(9-phenylcarbazol-3-yl)benzene-1,3,5-triamine (abbreviation: PCA3B), 2-[N-(9-phenylcarbazol-3-yl)-N-phenylamino]spiro-9,9′-bifluorene (abbreviation: PCASF), 2-[N-(4-diphenylaminophenyl)-N-phenylamino]spiro-9,9′-bifluorene (abbreviation: DPASF), N,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine (abbreviation: YGA2F), N,N′-bis(3-methylphenyl)-N,N′-diphenyl-[1,1′-biphenyl]-4,4′-diamine (abbreviation: TPD), 4,4′-bis[N-(4-diphenylaminophenyl)-N-phenylamino]biphenyl (abbreviation: DPAB), N-(9,9-dimethyl-9H-fluoren-2-yl)-N-{9,9-dimethyl-2-[N-phenyl-N-(9,9-dimethyl-9H-fluoren-2-yl)amino]-9H-fluoren-7-yl}phenylamine (abbreviation: DFLADFL), 3-[N-(9-phenylcarbazol-3-yl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzPCA1), 3-[N-(4-diphenylaminophenyl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzDPA1), 3,6-bis[N-(4-diphenylaminophenyl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzDPA2), 4,4′-bis(N-{4-[N′-(3-methylphenyl)-N-phenylamino]phenyl}-N-phenylamino)biphenyl (abbreviation: DNTPD, 3,6-bis[N-(4-diphenylaminophenyl)-N-(1-naphthyl)amino]-9-phenylcarbazole (abbreviation: PCzTPN2), and 3,6-bis[N-(9-phenylcarbazol-3-yl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzPCA2).

Note that as for the first organic compound and the second organic compound, the present invention is not limited to the above examples. The combination is determined so that an exciplex can be formed, the emission spectrum of the exciplex overlaps with the absorption spectrum of the phosphorescent compound, and the peak of the emission spectrum of the exciplex has a longer wavelength than the peak of the absorption spectrum of the phosphorescent compound.

Note that in the case where a compound which is likely to accept electrons and a compound which is likely to accept holes are used for the first organic compound and the second organic compound, carrier balance can be controlled by the mixture ratio of the compounds. That is, another feature of one embodiment of the present invention is that the optimal carrier balance with which the probability of recombination of holes and electrons in the light-emitting layer and the emission efficiency are increased can be designed by setting the mixture ratio. In view of the carrier balance and formation of an exciplex, it is preferable that the amount of the first organic compound and that of the second organic compound be not significantly different. Specifically, the ratio of the first organic compound to the second organic compound is preferably 1:9 to 9:1.

Further, the exciplex may be formed at the interface between two layers. For example, when a layer containing the second organic compound and a layer containing the first organic compound are stacked, the exciplex is formed in the vicinity of the interface thereof. These two layers may be used as the light-emitting layer in one embodiment of the present invention. In that case, the phosphorescent compound is added to the vicinity of the interface. The phosphorescent compound may be added to one of the two layers or both.

The electron-transport layer 704 is a layer that contains a substance having a high electron-transport property. Examples of the substance having a high electron-transport property are metal complexes such as Alq₃, tris(4-methyl-8-quinolinolato)aluminum (abbreviation: Almq₃), bis(10-hydroxybenzo[h]quinolinato)beryllium (abbreviation: BeBq₂), BAlq, Zn(BOXh, and bis[2-(2-hydroxyphenyl)benzothiazolato]zinc (abbreviation: Zn(BTZ)₂). Other examples thereof are heteroaromatic compounds such as 2-(4-biphenylyl)-5-(4-tert-butylphenyl)-1,3,4-oxadiazole (abbreviation: PBD), 1,3-bis[5-(p-tert-butylphenyl)-1,3,4-oxadiazol-2-yl]benzene (abbreviation: OXD-7), 3-(4-tert-butylphenyl)-4-phenyl-5-(4-biphenylyl)-1,2,4-triazole (abbreviation: TAZ), 3-(4-tert-butylphenyl)-4-(4-ethylphenyl)-5-(4-biphenylyl)-1,2,4-triazole (abbreviation: p-EtTAZ), bathophenanthroline (abbreviation: BPhen), bathocuproine (abbreviation: BCP), 4,4′-bis(5-methylbenzoxazol-2-yl)stilbene (abbreviation: BzOs). Still other examples are high molecular compounds such as poly(2,5-pyridine-diyl) (abbreviation: PPy), poly[(9,9-dihexylfluorene-2,7-diyl)-co-(pyridine-3,5-diyl)] (abbreviation: PF-Py), and poly[(9,9-dioctylfluorene-2,7-diyl)-co-(2,2′-bipyridine-6,6′-diyl)] (abbreviation: PF-BPy). The substances mentioned here are mainly substances having an electron mobility of 10⁻⁶ cm²/Vs or more. Note that other than these substances, any substance that has a property of transporting more holes than electrons may be used for the electron-transport layer.

Further, the electron-transport layer is not limited to a single layer, and may be a stack of two or more layers containing any of the above substances.

The electron-injection layer 705 is a layer that contains a substance having a high electron-injection property. Examples of the substance that can be used for the electron-injection layer 705 are alkali metals, alkaline earth metals, and compounds thereof, such as lithium, cesium, calcium, lithium fluoride, cesium fluoride, calcium fluoride, and lithium oxide, rare earth metal compounds, such as erbium fluoride, and the above-mentioned substances used for the electron-transport layer 704.

Alternatively, a composite material formed by combining an organic compound and an electron donor (a donor) may be used for the electron-injection layer 705. Such a composite material, in which electrons are generated in the organic compound by the electron donor, has high electron-injection and electron-transport properties. The organic compound here is preferably a material excellent in transporting the generated electrons, and specifically any of the above substances (such as metal complexes and heteroaromatic compounds) for the electron-transport layer 704 can be used. As the electron donor, a substance having an electron-donating property to the organic compound may be used. Preferable specific examples of the electron donor are alkali metals, alkaline earth metals, and rare earth metals, such as lithium, cesium, magnesium, calcium, erbium, and ytterbium. Any of alkali metal oxides and alkaline earth metal oxides is preferable, examples of which are lithium oxide, calcium oxide, barium oxide, and the like, and a Lewis base such as magnesium oxide or an organic compound such as tetrathiafulvalene (abbreviation: TTF) can be used.

Note that the hole-injection layer 701, the hole-transport layer 702, the light-emitting layer 703, the electron-transport layer 704, and the electron-injection layer 705 which are mentioned above can each be formed by a method such as an evaporation method (including a vacuum evaporation method), an inkjet method, or a coating method.

A plurality of EL layers may be stacked between the first electrode 103 and the second electrode 108 as illustrated in FIG. 7B. In that case, a charge-generation layer 803 is preferably provided between a first EL layer 800 and a second EL layer 801 which are stacked. The charge-generation layer 803 can be formed using the above-described composite material. Further, the charge-generation layer 803 may have a stacked structure including a layer containing the composite material and a layer containing another material. In that case, as the layer containing another material, a layer containing an electron-donating substance and a substance with a high electron-transport property, a layer formed of a transparent conductive film, or the like can be used. As for a light-emitting element having such a structure, problems such as energy transfer and quenching hardly occur, and a light-emitting element which has both high emission efficiency and a long lifetime can be easily obtained owing to a wider choice of materials. Moreover, a light-emitting element which provides phosphorescence from one of the EL layers and fluorescence from the other of the EL layers can be readily obtained. This structure can be combined with any of the above-described structures of the EL layer.

Furthermore, by making emission colors of EL layers different, light of a desired color can be obtained from the light-emitting element as a whole. For example, the emission colors of first and second EL layers are complementary in a light-emitting element having the two EL layers, so that the light-emitting element can be made to emit white light as a whole. Further, the same applies to a light-emitting element having three or more EL layers.

As illustrated in FIG. 7C, the EL layer 102 may include the hole-injection layer 701, the hole-transport layer 702, the light-emitting layer 703, the electron-transport layer 704, an electron-injection buffer layer 706, an electron-relay layer 707, and a composite material layer 708 which is in contact with the second electrode 108, between the first electrode 103 and the second electrode 108.

It is preferable to provide the composite material layer 708 which is in contact with the second electrode 108, in which case damage caused to the EL layer 102 particularly when the second electrode 108 is formed by a sputtering method can be reduced. The composite material layer 708 can be formed using the above-described composite material in which an organic compound having a high hole-transport property contains an acceptor substance.

Further, by providing the electron-injection buffer layer 706, an injection barrier between the composite material layer 708 and the electron-transport layer 704 can be reduced; thus, electrons generated in the composite material layer 708 can be easily injected to the electron-transport layer 704.

For the electron-injection buffer layer 706, a substance having a high electron-injection property, such as an alkali metal, an alkaline earth metal, a rare earth metal, a compound of the above metal (e.g., an alkali metal compound (including an oxide such as lithium oxide, a halide, and a carbonate such as lithium carbonate or cesium carbonate), an alkaline earth metal compound (including an oxide, a halide, and a carbonate), or a rare earth metal compound (including an oxide, a halide, and a carbonate), can be used.

Further, in the case where the electron-injection buffer layer 706 contains a substance having a high electron-transport property and a donor substance, the donor substance is preferably added so that the mass ratio of the donor substance to the substance having a high electron-transport property is in the range from 0.001:1 to 0.1:1. Note that as the donor substance, an organic compound such as tetrathianaphthacene (abbreviation: TIN′), nickelocene, or decamethylnickelocene can be used as well as an alkali metal, an alkaline earth metal, a rare earth metal, and a compound of the above metal (e.g., an alkali metal compound (including an oxide such as lithium oxide, a halide, and a carbonate such as lithium carbonate or cesium carbonate), an alkaline earth metal compound (including an oxide, a halide, and a carbonate), and a rare earth metal compound (including an oxide, a halide, and a carbonate)). Note that as the substance having a high electron-transport property, a material similar to the material for the electron-transport layer 704 described above can be used.

Furthermore, it is preferable that the electron-relay layer 707 be formed between the electron-injection buffer layer 706 and the composite material layer 708. The electron-relay layer 707 is not necessarily provided; however, by providing the electron-relay layer 707 having a high electron-transport property, electrons can be rapidly transported to the electron-injection buffer layer 706.

The structure in which the electron-relay layer 707 is sandwiched between the composite material layer 708 and the electron-injection buffer layer 706 is a structure in which the acceptor substance contained in the composite material layer 708 and the donor substance contained in the electron-injection buffer layer 706 are less likely to interact with each other, and thus their functions hardly interfere with each other. Therefore, an increase in drive voltage can be prevented.

The electron-relay layer 707 contains a substance having a high electron-transport property and is formed so that the LUMO level of the substance having a high electron-transport property is located between the LUMO level of the acceptor substance contained in the composite material layer 708 and the LUMO level of the substance having a high electron-transport property contained in the electron-transport layer 704. In the case where the electron-relay layer 707 contains a donor substance, the donor level of the donor substance is also controlled so as to be located between the LUMO level of the acceptor substance contained in the composite material layer 708 and the LUMO level of the substance having a high electron-transport property contained in the electron-transport layer 704. As a specific value of the energy level, the LUMO level of the substance having a high electron-transport property contained in the electron-relay layer 707 is preferably higher than or equal to −5.0 eV, more preferably higher than or equal to −5.0 eV and lower than or equal to −3.0 eV.

As the substance having a high electron-transport property contained in the electron-relay layer 707, a phthalocyanine-based material or a metal complex having a metal-oxygen bond and an aromatic ligand is preferably used.

As the phthalocyanine-based material contained in the electron-relay layer 707, specifically, any of CuPc, a phthalocyanine tin(II) complex (SnPc), a phthalocyanine zinc complex (ZnPc), cobalt(II) phthalocyanine, β-form (CoPc), phthalocyanine iron (FePc), and vanadyl 2,9,16,23-tetraphenoxy-29H,31H-phthalocyanine (PhO-VOPc), is preferably used.

As the metal complex having a metal-oxygen bond and an aromatic ligand, which is contained in the electron-relay layer 707, a metal complex having a metal-oxygen double bond is preferably used. The metal-oxygen double bond has an acceptor property (a property of easily accepting electrons); thus, electrons can be transferred (donated and accepted) more easily. Further, the metal complex having a metal-oxygen double bond is considered stable. Thus, the use of the metal complex having the metal-oxygen double bond enables the light-emitting element to be driven more stably at low voltage.

As the metal complex having a metal-oxygen bond and an aromatic ligand, a phthalocyanine-based material is preferable. Specifically, any of vanadyl phthalocyanine (VOPc), a phthalocyanine tin(IV) oxide complex (SnOPc), and a phthalocyanine titanium oxide complex (TiOPc) is preferable because a metal-oxygen double bond is likely to act on another molecule in terms of a molecular structure and an acceptor property is high.

Note that as the phthalocyanine-based materials mentioned above, a phthalocyanine-based material having a phenoxy group is preferable. Specifically, a phthalocyanine derivative having a phenoxy group, such as PhO-VOPc, is preferable. The phthalocyanine derivative having a phenoxy group is soluble in a solvent and therefore has the advantage of being easy to handle during formation of a light-emitting element and the advantage of facilitating maintenance of an apparatus used for film formation.

The electron-relay layer 707 may further contain a donor substance. As the donor substance, an organic compound such as tetrathianaphthacene (abbreviation: TIN), nickelocene, or decamethylnickelocene can be used as well as an alkali metal, an alkaline earth metal, a rare earth metal, and a compound of the above metal (e.g., an alkali metal compound (including an oxide such as lithium oxide, a halide, and a carbonate such as lithium carbonate or cesium carbonate), an alkaline earth metal compound (including an oxide, a halide, and a carbonate), and a rare earth metal compound (including an oxide, a halide, and a carbonate)). When such a donor substance is contained in the electron-relay layer 707, electrons can be transferred easily and the light-emitting element can be driven at lower voltage.

In the case where a donor substance is contained in the electron-relay layer 707, other than the materials given above as the substance having a high electron-transport property, a substance having a LUMO level higher than the acceptor level of the acceptor substance contained in the composite material layer 708 can be used. Specifically, it is preferable to use a substance having a LUMO level higher than or equal to −5.0 eV, preferably higher than or equal to −5.0 eV and lower than or equal to −3.0 eV. As examples of such a substance, a perylene derivative, a nitrogen-containing condensed aromatic compound, and the like are given. Note that a nitrogen-containing condensed aromatic compound is preferably used for the electron-relay layer 707 because of its high stability.

Specific examples of the perylene derivative are 3,4,9,10-perylenetetracarboxylic dianhydride (abbreviation: PTCDA), 3,4,9,10-perylenetetracarboxylic-bis-benzimidazole (abbreviation: PTCBI), N,N′-dioctyl-3,4,9,10-perylenetetracarboxylic diimide (abbreviation: PTCDI-C8H), N,N′-dihexyl-3,4,9, 10-perylenetetracarboxylic diimide (abbreviation: Hex PTC), and the like.

Specific examples of the nitrogen-containing condensed aromatic compound are pirazino[2,3-f][1,10]phenanthroline-2,3-dicarbonitrile (abbreviation: PPDN), 2,3,6,7,10,11-hexacyano-1,4,5,8,9,12-hexaazatriphenylene (abbreviation: HAT(CN)₆), 2,3-diphenylpyrido[2,3-b]pyrazine (abbreviation: 2PYPR), 2,3-bis(4-fluorophenyl)pyrido[2,3-b]pyrazine (abbreviation: F2PYPR), and the like.

Besides, 7,7,8,8-tetracyanoquinodimethane (abbreviation: TCNQ), 1,4,5,8-naphthalenetetracarboxylic dianhydride (abbreviation: NTCDA), perfluoropentacene, copper hexadecafluorophthalocyanine (abbreviation: F₁₆CuPc), N,N′-bis(2,2,3,3,4,4,5,5,6,6,7,7,8,8,8-pentadecafluoroctyl)-1,4,5,8-naphthalenetetracarboxylic diimide (abbreviation: NTCDI-C8F), 3′,4′-dibutyl-5,5″-bis(dicyanomethylene)-5,5″-dihydro-2,2′:5′,2″-terthiophene (abbreviation: DCMT), methanofullerenes (e.g., [6,6]-phenyl C₆₁ butyric acid methyl ester), or the like can be used.

Note that in the case where a donor substance is contained in the electron-relay layer 707, the electron-relay layer 707 may be formed by a method such as co-evaporation of the substance having a high electron-transport property and the donor substance.

The hole-injection layer 701, the hole-transport layer 702, the light-emitting layer 703, and the electron-transport layer 704 may each be formed using the above-described materials.

As described above, the EL layer 102 of this embodiment can be formed.

In the above-described light-emitting element, a current flows due to a potential difference generated between the first electrode 103 and the second electrode 108 and holes and electrons recombine in the EL layer 102, so that light is emitted. Then, this light emission is extracted to the outside through either the first electrode 103 or the second electrode 108 or both. Therefore, either the first electrode 103 or the second electrode 108, or both, is an electrode having a property of transmitting visible light.

Note that the structure of layers provided between the first electrode 103 and the second electrode 108 is not limited to the above-described structure. A structure other than the above may alternatively be employed as long as a light-emitting region in which holes and electrons recombine is provided in a portion away from the first electrode 103 and the second electrode 108 so as to prevent quenching due to proximity of the light-emitting region to metal.

In other words, there is no particular limitation on a stack structure of the layers. A layer including a substance having a high electron-transport property, a substance having a high hole-transport property, a substance having a high electron-injection property, a substance having a high hole-injection property, a bipolar substance (a substance having a high electron-transport property and a high hole-transport property), a hole-blocking material, or the like may freely be combined with a light-emitting layer.

In the above-described manner, the light-emitting element of one embodiment of the present invention can be manufactured.

By the use of the light-emitting element described in this embodiment, a passive matrix light-emitting device or an active matrix light-emitting device in which driving of the light-emitting element is controlled by a transistor can be manufactured. Furthermore, the light-emitting device can be applied to an electronic device, a lighting device, or the like.

Note that this embodiment can be combined with any of the other embodiments as appropriate.

Example 1

In this example, an example of a combination of a first organic compound, a second organic compound, and a phosphorescent compound which can be used for a light-emitting element of one embodiment of the present invention will be described with reference to FIG. 1, FIG. 2, FIG. 3, and FIG. 4.

The phosphorescent compound used in Structure Examples 1 to 4 in this example is (acetylacetonato)bis(4,6-diphenylpyrimidinato)iridium(II) (abbreviation: [Ir(dppm)₂(acac)]). The first organic compound used in Structure Examples 1 to 4 in this example is 2-[3-(dibenzothiophen-4-yl)phenyl]dibenzo[f,h]quinoxaline (abbreviation: 2mDBTPDBq-II). As the second organic compound in this example, 4-phenyl-4′-(9-phenyl-9H-carbazol-3-yl)triphenylamine (abbreviation: PCBA1BP) is used in Structure Example 1; 3-[N-(1-naphthyl)-N-(9-phenylcarbazol-3-yl)amino]-9-phenylcarbazole (abbreviation: PCzPCN1), Structure Example 2; 4,4′,4″-tris[N-(1-naphthyl)-N-phenylamino]triphenylamine (abbreviation: 1′-TNATA or 1-TNATA), Structure Example 3; and 2,7-bis[N-(4-diphenylaminophenyl)-N-phenylamino]-spiro-9,9′-bifluorene (abbreviation: DPA2SF), Structure Example 4.

Chemical formulae of materials used in this example are shown below.

Structure Example 1

FIG. 1 shows an emission spectrum of a thin film of 2mDBTPDBq-II that is the first organic compound (an emission spectrum 1 a), an emission spectrum of a thin film of PCBA1BP that is the second organic compound (an emission spectrum 2 a), and an emission spectrum of a thin film of a mixed material of 2mDBTPDBq-II and PCBA1BP (an emission spectrum 3 a). Further, an ultraviolet-visible absorption spectrum (hereinafter, simply referred to as absorption spectrum) and an emission spectrum (an emission spectrum 4 a) of [Ir(dppm)₂(acac)] that is the phosphorescent compound in a dichloromethane solution of [Ir(dppm)₂(acac)] are also shown.

Note that in this example, the absorption spectrum of [Ir(dppm)₂(acac)] was measured with the use of an ultraviolet-visible light spectrophotometer (V-550, manufactured by JASCO Corporation) in the state where the dichloromethane solution (0.093 mmol/L) was put in a quartz cell at room temperature.

In FIG. 1, the horizontal axis represents wavelength (nm), and the vertical axes represent molar absorption coefficient ε (M⁻¹·cm⁻¹) and emission intensity (arbitrary unit).

As can be seen from the absorption spectrum in FIG. 1, [Ir(dppm)₂(acac)] has a broad absorption band at around 510 nm. This absorption band is considered to greatly contribute to light emission.

The emission spectrum 3 a peaks at a longer wavelength than the emission spectra 1 a and 2 a. In addition, the peak of the emission spectrum 3 a is closer to the absorption band than the peaks of the emission spectra 1 a and 2 a. FIG. 1 shows that the emission spectrum 3 a has the largest overlap with the absorption band in the absorption spectrum which greatly contributes to light emission.

It is found that the emission spectrum of the mixed material of 2mDBTPDBq-II and PCBA1BP peaks at a longer wavelength than the emission spectrum of either organic compound alone. This indicates that an exciplex is formed by mixing 2mDBTPDBq-II with PCBA1BP.

It is found that the peak of the emission spectrum 3 a has a large overlap with the absorption band in the absorption spectrum of [Ir(dppm)₂(acac)] which is considered to greatly contribute to light emission. Thus, it is indicated that the light-emitting element including [Ir(dppm)₂(acac)] and the mixed material of 2mDBTPDBq-II and PCBA1BP has particularly high energy transfer efficiency because it transfers energy by utilizing the large overlap between the emission spectrum of the mixed material and the absorption spectrum of the phosphorescent compound. Accordingly, it is indicated that a light-emitting element having particularly high external quantum efficiency can be obtained.

Further, the peak of the emission spectrum 3 a is located on the longer wavelength side as compared to the peak of the absorption spectrum and is located on a shorter wavelength side as compared to the peak of the emission spectrum 4 a.

From the emission spectrum of the mixed material whose peak is located on the longer wavelength side, it is indicated that a light-emitting element having low drive voltage can be obtained with the use of the mixed material.

Structure Example 2

FIG. 2 shows an emission spectrum of a thin film of 2mDBTPDBq-II that is the first organic compound (an emission spectrum 1 b), an emission spectrum of a thin film of PCzPCN1 that is the second organic compound (an emission spectrum 2 b), and an emission spectrum of a thin film of a mixed material of 2mDBTPDBq-II and PCzPCN1 (an emission spectrum 3 b). Further, an absorption spectrum and an emission spectrum (an emission spectrum 4 b) of [Ir(dppm)₂(acac)] that is the phosphorescent compound in a dichloromethane solution of [Ir(dppm)₂(acac)] are also shown.

In FIG. 2, the horizontal axis represents wavelength (nm), and the vertical axes represent molar absorption coefficient ε (M⁻¹·cm⁻¹) and emission intensity (arbitrary unit).

As can be seen from the absorption spectrum in FIG. 2, [Ir(dppm)₂(acac)] has a broad absorption band at around 510 nm. This absorption band is considered to greatly contribute to light emission.

The emission spectrum 3 b peaks at a longer wavelength than the emission spectra 1 b and 2 b. That is, it is found that the emission spectrum of the mixed material of 2mDBTPDBq-II and PCzPCN1 peaks at a longer wavelength than the emission spectrum of either organic compound alone. This indicates that an exciplex is formed by mixing 2mDBTPDBq-II with PCzPCN1.

Further, the peak of the emission spectrum 3 b has an overlap with the absorption spectrum of [Ir(dppm)₂(acac)]. Thus, it is indicated that the light-emitting element including [Ir(dppm)₂(acac)] and the mixed material of 2mDBTPDBq-II and PCzPCN1 has high energy transfer efficiency because it transfers energy by utilizing the overlap between the emission spectrum of the mixed material and the absorption spectrum of the phosphorescent compound. Accordingly, it is indicated that a light-emitting element having high external quantum efficiency can be obtained.

Further, the peak of the emission spectrum 3 b is located on the longer wavelength side as compared to the peak of the absorption spectrum and is located on a shorter wavelength side as compared to the peak of the emission spectrum 4 b. In addition, the difference between the peak of the emission spectrum 3 b and that of the emission spectrum 4 b is 21 nm, which is very small.

From the emission spectrum of the mixed material whose peak is located on the particularly long wavelength side, it is indicated that a light-emitting element having particularly low drive voltage can be obtained with the use of the mixed material.

Structure Example 3

FIG. 3 shows an emission spectrum of a thin film of 2mDBTPDBq-II that is the first organic compound (an emission spectrum 1 c), an emission spectrum of a thin film of 1′-TNATA that is the second organic compound (an emission spectrum 2 c), and an emission spectrum of a thin film of a mixed material of 2mDBTPDBq-II and 1′-TNATA (an emission spectrum 3 c). Further, an absorption spectrum and an emission spectrum (an emission spectrum 4 c) of [Ir(dppm)₂(acac)] that is the phosphorescent compound in a dichloromethane solution of [Ir(dppm)₂(acac)] are also shown.

In FIG. 3, the horizontal axis represents wavelength (nm), and the vertical axes represent molar absorption coefficient ε (M⁻¹·cm⁻¹) and emission intensity (arbitrary unit).

As can be seen from the absorption spectrum in FIG. 3, [Ir(dppm)₂(acac)] has a broad absorption band at around 510 nm. This absorption band is considered to greatly contribute to light emission.

The emission spectrum 3 c peaks at a longer wavelength than the emission spectra 1 c and 2 c. That is, it is found that the emission spectrum of the mixed material of 2mDBTPDBq-II and 1′-TNATA peaks at a longer wavelength than the emission spectrum of either organic compound alone. This indicates that an exciplex is formed by mixing 2mDBTPDBq-II with 1′-TNATA.

Further, it is found that the peak of the emission spectrum 3 c has an overlap with the absorption spectrum of [Ir(dppm)₂(acac)]. Thus, it is indicated that the light-emitting element including [Ir(dppm)₂(acac)] and the mixed material of 2mDBTPDBq-II and 1′-TNATA has high energy transfer efficiency because it transfers energy by utilizing the overlap between the emission spectrum of the mixed material and the absorption spectrum of the phosphorescent compound. Accordingly, it is indicated that a light-emitting element having high external quantum efficiency can be obtained.

Further, the peak of the emission spectrum 3 c is located on the longer wavelength side as compared to the peak of the absorption spectrum. In addition, the difference between the peak of the emission spectrum 3 c and that of the emission spectrum 4 c is 24 nm, which is very small.

It can be considered that in the light-emitting element using the mixed material, a value of voltage with which an exciplex is formed through carrier recombination is smaller than a value of voltage with which the phosphorescent compound starts to emit light by carrier recombination. In other words, even when voltage that has a value smaller than that of voltage with which the phosphorescent compound starts to emit light is applied to the light-emitting element, carrier recombination occurs to form an exciplex and thus, current starts to flow in the light-emitting element. Thus, it is indicated that a light-emitting element having particularly low drive voltage can be obtained.

Structure Example 4

FIG. 4 shows an emission spectrum of a thin film of 2mDBTPDBq-II that is the first organic compound (an emission spectrum 1 d), an emission spectrum of a thin film of DPA2SF that is the second organic compound (an emission spectrum 2 d), and an emission spectrum of a thin film of a mixed material of 2mDBTPDBq-II and DPA2SF (an emission spectrum 3 d). Further, an absorption spectrum and an emission spectrum (an emission spectrum 4 d) of [Ir(dppm)₂(acac)] that is the phosphorescent compound in a dichloromethane solution of [Ir(dppm)₂(acac)] are also shown.

In FIG. 4, the horizontal axis represents wavelength (nm), and the vertical axes represent molar absorption coefficient ε (M⁻¹·cm⁻¹) and emission intensity (arbitrary unit).

As can be seen from the absorption spectrum in FIG. 4, [Ir(dppm)₂(acac)] has a broad absorption band at around 510 nm. This absorption band is considered to greatly contribute to light emission.

The emission spectrum 3 d peaks at a longer wavelength than the emission spectra 1 d and 2 d. That is, it is found that the emission spectrum of the mixed material of 2mDBTPDBq-II and DPA2SF peaks at a longer wavelength than the emission spectrum of either organic compound alone. This indicates that an exciplex is formed by mixing 2mDBTPDBq-II with DPA2SF.

Further, it is found that the peak of the emission spectrum 3 d has an overlap with the absorption spectrum of [Ir(dppm)₂(acac)]. Thus, it is indicated that the light-emitting element including [Ir(dppm)₂(acac)] and the mixed material of 2mDBTPDBq-II and DPA2SF has high energy transfer efficiency because it transfers energy by utilizing the overlap between the emission spectrum of the mixed material and the absorption spectrum of the phosphorescent compound. Accordingly, it is indicated that a light-emitting element having high external quantum efficiency can be obtained.

Further, the peak of the emission spectrum 3 d is located on the longer wavelength side as compared to the peak of the absorption spectrum. In addition, the difference between the peak of the emission spectrum 3 d and that of the emission spectrum 4 d is 13 nm, which is very small.

From the emission spectrum of the mixed material whose peak is located on at the particularly long wavelength side, it is indicated that a light-emitting element having particularly low drive voltage can be obtained with the use of the mixed material.

Example 2

In this example, a light-emitting element of one embodiment of the present invention will be described with reference to FIG. 8. Chemical formulae of materials used in this example are shown below. Note that the chemical formulae of the materials used in the above examples are omitted here.

Methods for manufacturing light-emitting elements 1 to 4 of this example will be described below.

(Light-Emitting Element 1)

First, a film of indium tin oxide containing silicon oxide (ITSO) was formed over a glass substrate 1100 by a sputtering method, so that a first electrode 1101 functioning as an anode was formed. Note that the thickness was set to 110 nm and the electrode area was set to 2 mm×2 mm.

Next, as pretreatment for forming the light-emitting element over the substrate 1100, UV ozone treatment was performed for 370 seconds after washing of a surface of the substrate with water and baking that was performed at 200° C. for one hour.

After that, the substrate was transferred into a vacuum evaporation apparatus where the pressure had been reduced to approximately 10⁻⁴ Pa, and was subjected to vacuum baking at 170° C. for 30 minutes in a beating chamber of the vacuum evaporation apparatus, and then the substrate 1100 was cooled down for about 30 minutes.

Next, the substrate 1100 provided with the first electrode 1101 was fixed to a substrate holder in the vacuum evaporation apparatus so that a surface on which the first electrode 1101 was provided faced downward. The pressure in the vacuum evaporation apparatus was reduced to about 10⁻⁴ Pa. Then, 4,4′,4″-(1,3,5-benzenetriyl)tri(dibenzothiophene) (abbreviation: DBT3P-II) and molybdenum(VI) oxide were co-evaporated to form a hole-injection layer 1111 over the first electrode 1101. The thickness of the hole-injection layer 1111 was set to 40 nm, and the mass ratio of DBT3P-II to molybdenum oxide was adjusted to 1:0.5 (=DBT3P-II: molybdenum oxide).

Next, over the hole-injection layer 1111, a film of PCBA1BP was formed to a thickness of 20 nm to form a hole-transport layer 1112.

Furthermore, 2mDBTPDBq-II, PCBA1BP, and [Ir(dppm)₂(acac)] were co-evaporated to form a light-emitting layer 1113 over the hole-transport layer 1112. Here, the weight ratio of 2mDBTPDBq-II to PCBA1BP and [Ir(dppm)₂(acac)] was adjusted to 0.7:03:0.05 (=2mDBTPDBq-II:PCBA1BP:[Ir(dppm)₂(acac)]). The thickness of the light-emitting layer 1113 was set to 40 nm.

Further, over the light-emitting layer 1113, a film of 2mDBTPDBq-II was formed to a thickness of 10 nm to form a first electron-transport layer 1114 a.

Next, over the first electron-transport layer 1114 a, a film of bathophenanthroline (abbreviation: BPhen) was formed to a thickness of 20 nm to form a second electron-transport layer 1114 b.

Further, over the second electron-transport layer 1114 b, a film of lithium fluoride (LiF) was formed by evaporation to a thickness of 1 nm to form an electron-injection layer 1115.

Lastly, an aluminum film was formed by evaporation to a thickness of 200 nm as a second electrode 1103 functioning as a cathode. Thus, the light-emitting element 1 of this example was fabricated.

(Light-Emitting Element 2)

The hole-transport layer 1112 of the light-emitting element 2 was formed by forming a film of PCzPCN1 to a thickness of 20 nm.

The light-emitting layer 1113 of the light-emitting element 2 was formed by co-evaporating 2mDBTPDBq-II, PCzPCN1, and [Ir(dppm)₂(acac)]. Here, the weight ratio of 2mDBTPDBq-II to PCzPCN1 and [Ir(dppm)₂(acac)] was adjusted to 0.7:0.3:0.05 (=2mDBTPDBq-II:PCzPCN1:[Ir(dppm)₂(acac)]). The thickness of the light-emitting layer 1113 was set to 40 nm. Components other than the light-emitting layer 1113 were manufactured in a manner similar to that of the light-emitting element 1.

(Light-Emitting Element 3)

The hole-transport layer 1112 of the light-emitting element 3 was formed by forming a film of 1′-TNATA to a thickness of 20 nm.

The light-emitting layer 1113 of the light-emitting element 3 was formed by co-evaporating 2mDBTPDBq-II, 1′-TNATA, and [Ir(dppm)₂(acac)]. Here, the weight ratio of 2mDBTPDBq-II to 1′-TNATA and [Ir(dppm)₂(acac)] was adjusted to 0.7:0.3:0.05 (=2mDBTPDBq-II:1′-TNATA:[Ir(dppm)₂(acac)]). The thickness of the light-emitting layer 1113 was set to 40 nm. Components other than the light-emitting layer 1113 were manufactured in a manner similar to that of the light-emitting element 1.

(Light-Emitting Element 4)

The hole-transport layer 1112 of the light-emitting element 4 was formed by forming a film of DPA2SF to a thickness of 20 nm.

The light-emitting layer 1113 of the light-emitting element 4 was formed by co-evaporating 2mDBTPDBq-II, DPA2SF, and [Ir(dppm)₂(acac)]. Here, the weight ratio of 2mDBTPDBq-II to DPA2SF and [Ir(dppm)₂(acac)] was adjusted to 0.7:0.3:0.05 (=2mDBTPDBq-II:DPA2SF:[Ir(dppm)₂(acac)]). The thickness of the light-emitting layer 1113 was set to 40 nm. Components other than the light-emitting layer 1113 were manufactured in a manner similar to that of the light-emitting element 1.

Note that, in all the above evaporation steps, evaporation was performed by a resistance-heating method.

Table 1 shows element structures of the light-emitting elements 1 to 4 obtained as described above.

TABLE 1 Second First Hole- Electron- Electron- Second Elec- Hole-injection transport First Electron- transport injection Elec- trode Layer Layer Light-emitting Layer transport Layer Layer Layer trode Light- ITSO DBT3P-II:MoOx PCBA1BP 2mDBTPDBq-II:PCBA1BP:[Ir(dppm)₂(acac)] 2mDBTPDBq- BPhen LiF Al emitting 110 nm (=1:0.5) 20 nm (=0.7:0.3:0.05) II 20 nm 1 nm 200 nm Element 1 40 nm 40 nm 10 nm Light- ITSO DBT3P-II:MoOx PCzPCN1 2mDBTPDBq-II:PCzPCN1:[Ir(dppm)₂(acac)] 2mDBTPDBq- BPhen LiF Al emitting 110 nm (=1:0.5) 20 nm (=0.7:0.3:0.05) II 20 nm 1 nm 200 nm Element 2 40 nm 40 nm 10 nm Light- ITSO DBT3P-II:MoOx P-TNATA 2mDBTPDBq-II:P-TNATA:[Ir(dppm)₂(acac)] 2mDBTPDBq- BPhen LiF Al emitting 110 nm (=1:0.5) 20 nm (=0.7:0.3:0.05) II 20 nm 1 nm 200 nm Element 3 40 nm 40 nm 10 nm Light- ITSO DBT3P-II:MoOx DPA2SF 2mDBTPDBq-II:P-DPA2SF:[Ir(dppm)₂(acac)] 2mDBTPDBq- BPhen LiF Al emitting 110 nm (=1:0.5) 20 nm (=0.7:0.3:0.05) II 20 nm 1 nm 200 nm Element 4 40 nm 40 nm 10 nm

In a glove box containing a nitrogen atmosphere, these light-emitting elements were sealed so as not to be exposed to air. Then, operation characteristics of these light-emitting elements were measured. Note that the measurements were carried out at room temperature (in the atmosphere kept at 25° C.).

FIG. 9 shows voltage-luminance characteristics of the light-emitting elements 1 to 4. In FIG. 9, the horizontal axis represents voltage (V), and the vertical axis represents luminance (cd/m²). Further, FIG. 10 shows voltage-current characteristics. In FIG. 10, the horizontal axis represents voltage (V), and the vertical axis represents current (mA). FIG. 11 shows luminance-power efficiency characteristics thereof. In FIG. 11, the horizontal axis represents luminance (cd/m²), and the vertical axis represents power efficiency (lm/W). FIG. 12 shows luminance-external quantum efficiency characteristics thereof. In FIG. 12, the horizontal axis represents luminance (cd/m²), and the vertical axis represents external quantum efficiency (%).

Further, Table 2 shows the voltage (V), current density (mA/cm²), CIE chromaticity coordinates (x, y), current efficiency (cd/A), power efficiency (lm/W), and external quantum efficiency (%) of each of the light-emitting elements 1 to 4 at a luminance of around 1000 cd/m².

TABLE 2 External Current Current Power Quantum Voltage Density Chromaticity Luminance Efficiency Efficiency Efficiency (V) (mA/cm²) (x, y) (cd/m²) (cd/A) (lm/W) (%) Light-emitting 2.7 1.5 (0.56, 0.44) 1000 68 79 27 Element 1 Light-emitting 2.5 1.6 (0.56, 0.43) 1000 67 84 26 Element 2 Light-emitting 2.7 2.3 (0.56, 0.43) 780 34 39 14 Element 3 Light-emitting 2.4 1.3 (0.56, 0.43) 800 62 81 25 Element 4

FIG. 13 shows emission spectra of the light-emitting elements 1 to 4 which were obtained by applying a current of 0.1 mA. In FIG. 13, the horizontal axis represents wavelength (nm), and the vertical axis represents emission intensity (arbitrary unit). As shown in Table 2, the CIE chromaticity coordinates of the light-emitting element 1 at a luminance of 1000 cd/m² were (x, y)=(0.56, 0.44); the CIE chromaticity coordinates of the light-emitting element 2 at a luminance of 1000 cd/m² were (x, y)=(0.56, 0.43); the CIE chromaticity coordinates of the light-emitting element 3 at a luminance of 780 cd/m² were (x, y)=(0.56, 0.43); and the CIE chromaticity coordinates of the light-emitting element 4 at a luminance of 800 cd/m² were (x, y)=(0.56, 0.43). These results show that orange light emission originating from [Ir(dppm)₂(acac)] was obtained from the light-emitting elements 1 to 4.

As can be seen from Table 2, FIG. 11, and FIG. 12, the light-emitting elements 1 to 4 have high current efficiency, high power efficiency, and high external quantum efficiency.

In the light-emitting elements of this example, the first organic compound, the second organic compound, and the guest material which are described in Example 1 are used for the light-emitting layer. As described in Example 1, the emission spectrum of the mixed material of 2mDBTPDBq-II and the second organic compound (the emission spectrum of an exciplex) overlaps with the absorption spectrum of [Ir(dppm)₂(acac)]. The light-emitting elements of this example are considered to have high energy transfer efficiency because it transfers energy by utilizing the overlap, and therefore have high external quantum efficiency.

In this example, the light-emitting elements 1, 2, and 4 have higher external quantum efficiency than the light-emitting element 3 (see FIG. 12). The reason for this is considered that the light-emitting elements 1, 2, and 4 each have a larger overlap between the emission spectrum of the exciplex and the absorption spectrum of [Ir(dppm)₂(acac)] than the light-emitting element 3 (refer to FIG. 1, FIG. 2, FIG. 3, FIG. 4, and Example 1).

As can be seen from FIG. 9 and FIG. 10, the light-emitting elements 1 to 4 have low emission start voltage. The theoretical value of emission start voltage of an orange emissive organic EL element is said to be approximately 2.1 V, to which the emission start voltage of the light-emitting element of one embodiment of the present invention was found to be extremely close.

In this example, the light-emitting elements 2 to 4 have lower emission start voltage than the light-emitting element 1 (see FIG. 10 and FIG. 11). The reason for this is considered that the emission spectrum of the exciplex of each of the light-emitting elements 2 to 4 peaks at a longer wavelength than the emission spectrum of the exciplex of the light-emitting element 1 (refer to FIG. 1, FIG. 2, FIG. 3, FIG. 4, and Example 1).

The above results show that an element having high external quantum efficiency can be obtained by application of one embodiment of the present invention. Moreover, it is shown that an element having low drive voltage can be obtained by application of one embodiment of the present invention.

Next, the light-emitting element 4 was subjected to reliability tests. Results of the reliability tests are shown in FIG. 14. In FIG. 14, the vertical axis represents normalized luminance (%) with an initial luminance of 100%, and the horizontal axis represents driving time (h) of the element.

In the reliability tests, the light-emitting element 4 was driven under the conditions where the initial luminance was set to 5000 cd/m² and the current density was constant.

The luminance of the light-emitting element 4 after 260 hours was 93% of the initial luminance. From the results, the light-emitting element 4 is found to have a long lifetime.

The above results show that an element having low drive voltage and high reliability can be obtained by application of one embodiment of the present invention.

Example 3

In this example, a light-emitting element of one embodiment of the present invention will be described. Chemical formulae of the materials used in this example are shown below. Note that the chemical formulae of the materials used in the above examples are omitted here.

Light-emitting elements formed in this example are Structure Examples a to s. An element structure of the Structure Examples a to s is shown in Table 3. Note that the Structure Examples a to s are different from one another in a substance X used in hole-transport layers and light-emitting layers. Names of the substances X used in the structure examples are shown below. Further, Table 4 shows the HOMO levels (eV) of the substances X used in the structure examples and emission peak wavelengths (nm) of exciplexes formed in the structure examples. Note that in this example, a photoelectron spectrometer (AC-2, product of Riken Keiki Co., Ltd.) was used to measure the HOMO level.

TABLE 3 Second First Hole- Hole- Electron- Electron- Elec- injection transport First Electron- transport injection Second trode Layer Layer Light-emitting Layer transport Layer Layer Layer Electrode Light- ITSO DBT3P- Substance X 2mDBTPDBq-II:Substance X:[Ir(dppm)₂(acac)] 2mDBTPDBq-II BPhen LiF Al emitting 110 nm II:MoOx 20 nm (=0.7:0.3:0.05) 10 nm 20 nm 1 nm 200 nm Element (=1:0.5) 40 nm 40 nm

TABLE 4 Peak Wavelength of HOMO Level of Emission Spectrum of Structure Substance X Exciplex Example Substance X (eV) (nm) a PCBA1BP −5.42 519 b PCA2B −5.40 546 c DPNF −5.35 555 d PCA3B −5.31 553 e PCASF −5.30 543 f DPASF −5.30 571 g YGA2F −5.27 540 h TPD −5.25 537 i DPAB −5.23 573 j DFLADFL −5.20 557 k PCzPCA1 −5.17 571 l PCzDPA1 −5.16 581 m PCzDPA2 −5.16 586 n PCzPCN1 −5.15 571 o DNTPD −5.14 573 p PCzTPN2 −5.13 582 q DPA2SF −5.09 579 r 1′-TNATA −5.09 616 s PCzPCA2 −5.08 575

Structure Example a

The Structure Example a is the light-emitting element 1 described in Example 2. PCBA1BP was used as the substance X.

Structure Example b

N,N′-bis(9-phenylcarbazol-3-yl)-N,N′-diphenylbenzene-1,3-diamine (abbreviation: PCA2B) was used as the substance X.

Structure Example c

As the substance X was used N-(9,9-dimethyl-2-N,N-diphenylamino-9H-fluoren-7-yl)diphenylamine (abbreviation: DPNF).

Structure Example d

N,N′,N″-triphenyl-N,N′,N″-tris(9-phenylcarbazol-3-yl)benzene-1,3,5-triamine (abbreviation: PCA3B) was used as the substance X.

Structure Example e

As the substance X was used 2-[N-(9-phenylcarbazol-3-yl)-N-phenylamino]spiro-9,9′-bifluorene (abbreviation: PCASF).

Structure Example f

As the substance X was used 2-[N-(4-diphenylaminophenyl)-N-phenylamino]spiro-9,9′-bifluorene (abbreviation: DPASF).

Structure Example g

N,N′-bis[4-(carbazol-9-yl)phenyl]-N,N-diphenyl-9,9-dimethylfluorene-2,7-diamine (abbreviation: YGA2F) was used as the substance X.

Structure Example h

As the substance X was used N,N′-bis(3-methylphenyl)-N,N′-diphenyl-[1,1′-biphenyl]-4,4′-diamine (abbreviation: TPD).

Structure Example i

As the substance X was used 4,4′-bis[N-(4-diphenylaminophenyl)-N-phenylamino]biphenyl (abbreviation: DPAB).

Structure Example j

N-(9,9-dimethyl-9H-fluoren-2-yl)-N-{9,9-dimethyl-2-[N-phenyl-N-(9,9-dimethyl-9H-fluoren-2-yl)amino]-9H-fluoren-7-yl}phenylamine (abbreviation: DFLADFL) was used as the substance X.

Structure Example k

As the substance X was used 3-[N-(9-phenylcarbazol-3-yl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzPCA1).

Structure Example l

As the substance X was used 3-[N-(4-diphenylaminophenyl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzDPA1).

Structure Example m

As the substance X was used 3,6-bis[N-(4-diphenylaminophenyl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzDPA2).

Structure Example n

The Structure Example n is the light-emitting element 2 described in Example 2. PCzPCN1 was used as the substance X.

Structure Example o

As the substance X was used 4,4′-bis(N-{4-[N-(3-methylphenyl)-N′-phenylamino]phenyl}-N-phenylamino)biphenyl (abbreviation: DNTPD).

Structure Example p

As the substance X was used 3,6-bis[N-(4-diphenylaminophenyl)-N-(1-naphthyl)amino]-9-phenylcarbazole (abbreviation: PCzTPN2).

Structure Example q

The Structure Example q is the light-emitting element 4 described in Example 2. DPA2SF was used as the substance X.

Structure Example r

The Structure Example r is the light-emitting element 3 described in Example 2. As the substance X, 1′-TNATA was used.

Structure Example s

As the substance X was used 3,6-bis[N-(9-phenylcarbazol-3-yl)-N-phenylamino]-9-phenylcarbazole (abbreviation: PCzPCA2).

FIG. 15 shows a relationship between the peak wavelength of the emission spectrum of the exciplex and the HOMO level of the substance X in each structure example. In FIG. 15, the horizontal axis represents the peak wavelength (nm) and the vertical axis represents the HOMO level (eV). Further, FIG. 16 shows a relationship between the peak wavelength of the emission spectrum of the exciplex and relative external quantum efficiency in each structure example. In FIG. 16, the horizontal axis represents the peak wavelength (nm) and the vertical axis represents the relative external quantum efficiency (arbitrary unit). Note that the relative external quantum efficiency in FIG. 16 is shown as a value relative to the external quantum efficiency of the light-emitting element in the Structure Example a assumed to be 1. In FIG. 16, relative external quantum efficiency of the Structure Example e and the Structure Example h is not shown.

It is indicated from FIG. 15 that when the HOMO level of the substance X is higher, the emission spectrum of the exciplex formed from 2mDBTPDBq-II and the substance X peaks at a longer wavelength. Therefore, when the HOMO level of the substance X is higher and the emission spectrum of the exciplex peaks at a longer wavelength, the emission start voltage of the light-emitting element can be lower. Accordingly, the light-emitting element can have lower drive voltage.

From FIG. 16, it can be seen that the external quantum efficiency of the light-emitting element is low when the peak wavelength of the emission spectrum of the exciplex is too long. What is indicated is that the peak wavelength of the emission spectrum of the exciplex has a preferable range for high external quantum efficiency and low drive voltage of a light-emitting element. Specifically, it is indicated that in order that both low drive voltage and high external quantum efficiency be achieved, the peak wavelength of the emission spectrum of the exciplex is preferably longer than or equal to the peak wavelength (in this example, approximately 510 nm in the absorption spectrum of the phosphorescent compound in a solution) of the absorption band located on the longest wavelength side of the absorption spectrum of the phosphorescent compound, and preferably shorter than or equal to the peak wavelength (in this example, approximately 580 nm in an emission spectrum of electroluminescence) of the emission spectrum of the phosphorescent compound.

Reference Example 1

A synthetic example of an organometallic complex (acetylacetonato)bis(4,6-diphenylpyrimidinato)iridium(III) (another name: bis[2-(6-phenyl-4-pyrimidinyl-κN3)phenyl-κC](2,4-pentanedionato-κ²O,O′)iridium(III)) (abbreviation: [Ir(dppm)₂(acac)], which is used in the above examples, is described. The structure of [Ir(dppm)₂(acac)] is shown below.

Step 1: Synthesis of 4,6-Diphenylpyrimidine (Abbreviation: Hdppm)

First, 5.02 g of 4,6-dichloropyrimidine, 8.29 g of phenylboronic acid, 7.19 g of sodium carbonate, 0.29 g of bis(triphenylphosphine)palladium(II)dichloride (abbreviation: Pd(PPh₃)₂Cl₂), 20 mL of water, and 20 mL of acetonitrile were put into a recovery flask equipped with a reflux pipe, and the air in the flask was replaced with argon. This reaction container was heated by irradiation with microwaves (2.45 GHz, 100 W) for 60 minutes. Here, there were further put 2.08 g of phenylboronic acid, 1.79 g of sodium carbonate, 0.070 g of Pd(PPh₃)₂Cl₂, 5 mL of water, and 5 mL of acetonitrile into the flask, and the mixture was heated again by irradiation with microwaves (2.45 GHz, 100 W) for 60 minutes. After that, water was added to this solution and an organic layer was extracted with dichloromethane. The obtained solution of the extract was washed with water and dried with magnesium sulfate. The solution after drying was filtered. The solvent of this solution was distilled off, and then the obtained residue was purified by silica gel column chromatography using dichloromethane as a developing solvent, so that a pyrimidine derivative Hdppm (yellow white powder, yield of 38%) was obtained. Note that for the irradiation with microwaves, a microwave synthesis system (Discover, manufactured by CEM Corporation) was used. A synthesis scheme (a-1) of Step I is shown below.

Step 2: Synthesis of Di-μ-chloro-bis[bis(4,6-diphenylpyrimidinato)iridium(III)] (abbreviation: [Ir(dppm)₂Cl]₂)

Next, 15 mL of 2-ethoxyethanol, 5 mL of water, 1.10 g of Hdppm obtained in Step 1, and 0.69 g of iridium chloride hydrate (IrCl₃.H₂O) were put into a recovery flask equipped with a reflux pipe, and the air in the recovery flask was replaced with argon. After that, irradiation with microwaves (2.45 GHz, 100 W) was performed for 1 hour to cause a reaction. The solvent was distilled off and then the obtained residue was filtered and washed with ethanol to give a dinuclear complex [Ir(dppm)₂Cl]₂ (reddish brown powder, yield of 88%). A synthesis scheme (a-2) of Step 2 is shown below.

Step 3: Synthesis of (Acetylacetonato)bis(4,6-diphenylpyrimidinato)iridium(III) (abbreviation: [Ir(dppm)₂(acac)])

Furthermore, 40 mL of 2-ethoxyethanol, 1.44 g of [Ir(dppm)₂Cl]₂ obtained in Step 2, 0.30 g of acetylacetone, and 1.07 g of sodium carbonate were put into a recovery flask equipped with a reflux pipe, and the air in the recovery flask was replaced with argon. After that, irradiation with microwaves (2.45 GHz, 120 W) was performed for 60 minutes to cause a reaction. The solvent was distilled off, the obtained residue was dissolved in dichloromethane, and filtration was performed to remove insoluble matter. The obtained filtrate was washed with water and then with saturated saline, and was dried with magnesium sulfate. The solution after drying was filtered. The solvent of this solution was distilled off, and then the obtained residue was purified by silica gel column chromatography using dichloromethane and ethyl acetate as a developing solvent in a volume ratio of 50:1. After that, recrystallization was carried out with a mixed solvent of dichloromethane and hexane, so that the objective orange powder (yield of 32%) was obtained. A synthesis scheme (a-3) of Step 3 is shown below.

An analysis result by nuclear magnetic resonance spectrometry (¹H NMR) of the orange powder obtained in Step 3 is described below. These results revealed that the organometallic complex [Ir(dppm)₂(acac)] was obtained.

¹H NMR. δ (CDCl₃): 1.83 (s, 6H), 5.29 (s, 1H), 6.48 (d, 2H), 6.80 (t, 2H), 6.90 (t, 2H), 7.55-7.63 (m, 6H), 7.77 (d, 2H), 8.17 (s, 2H), 8.24 (d, 4H), 9.17 (s, 2H).

Reference Example 2

A method for synthesizing 2-[3-(dibenzothiophen-4-yl)phenyl]dibenzo[f,h]quinoxaline (abbreviation: 2mDBTPDBq-II), which is used in the above examples, is described.

Synthesis of 2-[3-(Dibenzothiophen-4-yl)phenyl]dibenzo[f,h]quinoxaline (abbreviation: 2mDBTPDBq-II)

A synthesis scheme (b-1) of 2-[3-(dibenzothiophen-4-yl)phenyl]dibenzo[f,h]quinoxaline (abbreviation: 2mDBTPDBq-II) is shown below.

First, 5.3 g (20 mmol) of 2-chlorodibenzo[f,h]quinoxaline, 6.1 g (20 mmol) of 3-(dibenzothiophen-4-yl)phenylboronic acid, 460 mg (0.4 mmol) of tetrakis(triphenylphosphine)palladium(0), 300 mL of toluene, 20 mL of ethanol, and 20 mL of a 2M aqueous solution of potassium carbonate were put in a 2 L three-neck flask. The mixture was degassed by being stirred under reduced pressure, and the air in the three-neck flask was replaced with nitrogen. This mixture was stirred under a nitrogen stream at 100° C. for 7.5 hours. After cooled to room temperature, the obtained mixture was filtered to give a white residue. The obtained residue was washed with water and ethanol in this order, and then dried. The obtained solid was dissolved in about 600 mL of hot toluene, followed by suction filtration through Celite (produced by Wako Pure Chemical Industries, Ltd., Catalog No. 531-16855) and Florisil (produced by Wako Pure Chemical Industries, Ltd., Catalog No. 540-00135), whereby a clear colorless filtrate was obtained. The obtained filtrate was concentrated and purified by silica gel column chromatography using about 700 mL of silica gel. The chromatography was carried out using hot toluene as a developing solvent Acetone and ethanol were added to the solid obtained here, followed by irradiation with ultrasonic waves. Then, the generated suspended solid was collected by filtration and the obtained solid was dried, so that 7.85 g of white powder was obtained in 80% yield.

The above objective substance was relatively soluble in hot toluene, but was a material that was likely to be precipitated when cooled. Further, the substance was poorly soluble in other organic solvents such as acetone and ethanol Hence, the utilization of these different degrees of solubility resulted in a high-yield synthesis by a simple method as above. Specifically, after the reaction finished, the mixture was returned to room temperature and the precipitated solid was collected by filtration, whereby most impurities were able to be easily removed. Further, by the column chromatography with hot toluene as a developing solvent, the objective substance, which is likely to be precipitated, was able to be readily purified.

By a train sublimation method, 4.0 g of the obtained white powder was purified. In the purification, the white powder was heated at 300° C. under a pressure of 5.0 Pa with a flow rate of argon gas of 5 ml/min. After the purification, the objective substance was obtained in a yield of 88% as 3.5 g of white powder.

A nuclear magnetic resonance spectrometry (¹H NMR) identified this compound as the objective 2-[3-(dibenzothiophen-4-yl)phenyl]dibenzo[f,h]quinoxaline (abbreviation: 2mDBTPDBq-II).

¹H NMR data of the obtained substance are shown below.

¹H NMR (CDCl₃, 300 MHz): δ (ppm)=7.45-7.52 (m, 2H), 7.59-7.65 (m, 2H), 7.71-7.91 (m, 7H), 8.20-8.25 (m, 2H), 8.41 (d, J=7.8 Hz, 1H), 8.65 (d, J=7.5 Hz, 2H), 8.77-8.78 (m, 1H), 9.23 (dd, J=7.2 Hz, 1.5 Hz, 1H), 9.42 (dd, J=7.8 Hz, 1.5 Hz, 1H), 9.48 (s, 1H).

REFERENCE NUMERALS

102: EL layer, 103: first electrode, 108: second electrode, 701: hole-injection layer, 702: hole-transport layer, 703: light-emitting layer, 704: electron-transport layer, 705: electron-injection layer, 706: electron-injection buffer layer, 707: electron-relay layer, 708: composite material layer, 800: first EL layer, 801: second EL layer, 803: charge generation layer, 1100: substrate, 1101: first electrode, 1103: second electrode, 1111: hole-injection layer, 1112: hole-transport layer, 1113: light-emitting layer, 1114 a: first electron-transport layer, 1114 b: second electron-transport layer, and 1115: electron-injection layer

This application is based on Japanese Patent Application serial no. 2011-064553 filed with Japan Patent Office on Mar. 23, 2011, the entire contents of which are hereby incorporated by reference. 

The invention claimed is:
 1. A light-emitting element comprising: a pair of electrodes; and a light-emitting layer comprising a first organic compound, a second organic compound and a phosphorescent compound between the pair of electrodes, wherein the first organic compound and the second organic compound are selected so as to form an exciplex, wherein an emission spectrum of the exciplex overlaps with an absorption band on the longest-wavelength-side in an absorption spectrum of the phosphorescent compound, wherein a peak wavelength of the emission spectrum of the exciplex is longer than or equal to a peak wavelength of the absorption band on the longest-wavelength-side in the absorption spectrum of the phosphorescent compound, and wherein one of the first organic compound and the second organic compound is a carbazole compound.
 2. The light-emitting element according to claim 1, wherein the first organic compound is a heteroaromatic compound.
 3. The light-emitting element according to claim 1, further comprising: a hole injection layer, wherein the hole injection layer comprises an aromatic amine and an electron acceptor.
 4. The light-emitting element according to claim 1, further comprising: a hole transport layer, wherein the hole transport layer comprises an aromatic amine having a fluorenyl group.
 5. The light-emitting element according to claim 1, further comprising: a hole transport layer, wherein the hole transport layer comprises an aromatic amine having a fluorenyl group.
 6. The light-emitting element according to claim 1, further comprising: a hole transport layer, wherein the hole transport layer comprises an aromatic amine having a spiro-9,9′-bifluorene group.
 7. The light-emitting element according to claim 1, wherein one of the electrodes comprises ytterbium.
 8. The light-emitting element according to claim 1, wherein the absorption band on the longest-wavelength-side is an absorption wavelength corresponding to direct transition from a singlet ground state to a triplet excitation state.
 9. The light-emitting element according to claim 1, wherein a level of a triplet excitation energy of each of the first organic compound and second organic compound is higher than a level of a triplet excitation energy of the phosphorescent compound.
 10. The light-emitting element according to claim 1, wherein one of the first organic compound and the second organic compound has higher content than the other, and wherein a phosphorescence spectrum of the one overlaps with the absorption band on the longest-wavelength-side in the absorption spectrum of the phosphorescent compound.
 11. A light-emitting element comprising: a pair of electrodes; and a light-emitting layer comprising a phosphorescent compound, a first organic compound and a second organic compound between the pair of electrodes, wherein the first organic compound and the second organic compound are selected so as to form an exciplex, wherein an emission spectrum of the exciplex overlaps with an absorption band on the longest-wavelength-side in an absorption spectrum of the phosphorescent compound, wherein a difference between a peak wavelength of the emission spectrum of the exciplex and a peak wavelength of an emission spectrum of the phosphorescent compound is less than or equal to 30 nm, and wherein a peak wavelength of the emission spectrum of the exciplex is longer than or equal to a peak wavelength of the absorption band on the longest-wavelength-side in the absorption spectrum of the phosphorescent compound, and wherein one of the first organic compound and the second organic compound is a carbazole compound.
 12. The light-emitting element according to claim 11, wherein the first organic compound is a heteroaromatic compound.
 13. The light-emitting element according to claim 11, further comprising: a hole injection layer, wherein the hole injection layer comprises an aromatic amine and an electron acceptor.
 14. The light-emitting element according to claim 11, further comprising: a hole transport layer, wherein the hole transport layer comprises an aromatic amine having a fluorenyl group.
 15. The light-emitting element according to claim 11, further comprising: a hole transport layer, wherein the hole transport layer comprises an aromatic amine having a fluorenyl group.
 16. The light-emitting element according to claim 11, further comprising: a hole transport layer, wherein the hole transport layer comprises an aromatic amine having a spiro-9,9′-bifluorene group.
 17. The light-emitting element according to claim 11, wherein one of the electrodes comprises ytterbium.
 18. The light-emitting element according to claim 11, wherein the absorption band on the longest-wavelength-side is an absorption wavelength corresponding to direct transition from a singlet ground state to a triplet excitation state.
 19. The light-emitting element according to claim 11, wherein a level of a triplet excitation energy of each of the first organic compound and second organic compound is higher than a level of a triplet excitation energy of the phosphorescent compound.
 20. The light-emitting element according to claim 11, wherein one of the first organic compound and the second organic compound has higher content than the other, and wherein a phosphorescence spectrum of the one overlaps with the absorption band on the longest-wavelength-side in the absorption spectrum of the phosphorescent compound.
 21. A light-emitting element comprising: a pair of electrodes; and a light-emitting layer comprising a first organic compound, a second organic compound and a phosphorescent compound between the pair of electrodes, wherein the first organic compound and the second organic compound are selected so as to form an exciplex, wherein an emission spectrum of the exciplex overlaps with an absorption band on the longest-wavelength-side in an absorption spectrum of the phosphorescent compound, wherein a peak wavelength of the emission spectrum of the exciplex is longer than or equal to a peak wavelength of the absorption band on the longest-wavelength-side in the absorption spectrum of the phosphorescent compound, and wherein a level of a triplet excitation energy of each of the first organic compound and second organic compound is higher than a level of a triplet excitation energy of the phosphorescent compound.
 22. The light-emitting element according to claim 21, wherein the absorption band on the longest-wavelength-side is an absorption wavelength corresponding to direct transition from a singlet ground state to a triplet excitation state.
 23. The light-emitting element according to claim 21, wherein one of the first organic compound and the second organic compound has higher content than the other, and wherein a phosphorescence spectrum of the one overlaps with the absorption band on the longest-wavelength-side in the absorption spectrum of the phosphorescent compound. 